系统研究了室温下Tb0.3Dy0.7-xPrx(Fe0.9Al0.1)1.95(x=0,0.1,0.2,0.25,0.3,0.35)合金中稀土元素Pr替代Dy对晶体结构、磁致伸缩、各向异性和自旋重取向的影响.结果发现,x≤0.1时,Tb0.3Dy0.7-xPrx(Fe0.9Al0.1)1.95完全保持MgCl2立方Laves相结构,0.1＜x≤0.3,有杂相出现并且随Pr替代量逐渐增多;晶格常数a随Pr含量x的增加缓慢增大.磁致伸缩测量发现,随着替代量x的增多磁致伸缩减小;x＞0.2时超磁致伸缩效应消失.然而,x=0.1时合金的磁致伸缩略大于没有替代的,而且磁致伸缩随磁场更易趋于饱和,说明Pr替代有助于降低磁晶各向异性.内禀磁致伸缩λ111随Pr替代量x的增加接近线性增加.由相对磁化率随温度的变化关系可以看出,自旋重取向温度随Pr替代量的增多呈先增后降趋势,在x=0.1处出现极大值.穆斯堡尔效应表明,随Pr含量的增加Tb0.3Dy0.7-xPrx(Fe0.9Al0.1)1.95合金中易磁化轴可能在{110}面上绕主对称轴作微小转动,发生自旋重取向.与Al元素替代效应相比,Pr替代Dy对自旋重取向的影响相对较小.
계통연구료실온하Tb0.3Dy0.7-xPrx(Fe0.9Al0.1)1.95(x=0,0.1,0.2,0.25,0.3,0.35)합금중희토원소Pr체대Dy대정체결구、자치신축、각향이성화자선중취향적영향.결과발현,x≤0.1시,Tb0.3Dy0.7-xPrx(Fe0.9Al0.1)1.95완전보지MgCl2립방Laves상결구,0.1＜x≤0.3,유잡상출현병차수Pr체대량축점증다;정격상수a수Pr함량x적증가완만증대.자치신축측량발현,수착체대량x적증다자치신축감소;x＞0.2시초자치신축효응소실.연이,x=0.1시합금적자치신축략대우몰유체대적,이차자치신축수자장경역추우포화,설명Pr체대유조우강저자정각향이성.내품자치신축λ111수Pr체대량x적증가접근선성증가.유상대자화솔수온도적변화관계가이간출,자선중취향온도수Pr체대량적증다정선증후강추세,재x=0.1처출현겁대치.목사보이효응표명,수Pr함량적증가Tb0.3Dy0.7-xPrx(Fe0.9Al0.1)1.95합금중역자화축가능재{110}면상요주대칭축작미소전동,발생자선중취향.여Al원소체대효응상비,Pr체대Dy대자선중취향적영향상대교소.