SAPO-34 molecular sieve%template%crystal seed%crystallinity
在加入晶种的体系中,研究了模板剂用量、磷源用量和晶种加入量对合成SAPO-34分子筛的影响.实验结果表明,模板剂是形成SAPO-34分子筛骨架的必要条件;在加入适量模板剂的条件下,加入晶种可提高SAPO-34分子筛的结晶度;在一定范围内增大模板剂用量,可提高SAPO-34分子筛的结晶度,过量的模板剂反而会降低结晶度;降低磷源用量可增强晶种的作用、降低模板剂用量和缩短晶化时间;增加晶种加入量,能提高生成SAPO-34分子筛的选择性,当晶种干基与SiO_2质量比为0.39时,SAPO-5分子筛杂晶消失,得到纯SAPO-34分子筛,且晶化时间缩短了24 h,但晶种加入量达到一定值后,SAPO-34分子筛的结晶度不再明显增加.
在加入晶種的體繫中,研究瞭模闆劑用量、燐源用量和晶種加入量對閤成SAPO-34分子篩的影響.實驗結果錶明,模闆劑是形成SAPO-34分子篩骨架的必要條件;在加入適量模闆劑的條件下,加入晶種可提高SAPO-34分子篩的結晶度;在一定範圍內增大模闆劑用量,可提高SAPO-34分子篩的結晶度,過量的模闆劑反而會降低結晶度;降低燐源用量可增彊晶種的作用、降低模闆劑用量和縮短晶化時間;增加晶種加入量,能提高生成SAPO-34分子篩的選擇性,噹晶種榦基與SiO_2質量比為0.39時,SAPO-5分子篩雜晶消失,得到純SAPO-34分子篩,且晶化時間縮短瞭24 h,但晶種加入量達到一定值後,SAPO-34分子篩的結晶度不再明顯增加.
재가입정충적체계중,연구료모판제용량、린원용량화정충가입량대합성SAPO-34분자사적영향.실험결과표명,모판제시형성SAPO-34분자사골가적필요조건;재가입괄량모판제적조건하,가입정충가제고SAPO-34분자사적결정도;재일정범위내증대모판제용량,가제고SAPO-34분자사적결정도,과량적모판제반이회강저결정도;강저린원용량가증강정충적작용、강저모판제용량화축단정화시간;증가정충가입량,능제고생성SAPO-34분자사적선택성,당정충간기여SiO_2질량비위0.39시,SAPO-5분자사잡정소실,득도순SAPO-34분자사,차정화시간축단료24 h,단정충가입량체도일정치후,SAPO-34분자사적결정도불재명현증가.
SAPO-34 molecular sieves were synthesized in presence of crystal seed. Effects of dosages of the template, phosphorus source and crystal seed on the synthesis were investigated. The experiments showed that template was the key substance for formation of SAPO-34 framework. With a proper amount of template the addition of crystal seed enhanced the crystallinity of SAPO-34. Although increasing a certain amount of template could improve crystallinity of SAPO-34 to a certain extent, excess of it would contrarily cause undesirable result. Reducing the addition amount of phosphorus source material could bring the role of crystal seed into prominence, save some amount of template and shorten the crystallization time. Properly increasing the amount of crystal seed was preferable to selectivity to SAPO-34. When the mass ratio of crystal seed(dry basis) to SiO_2 was 0.39, the formation of miscellaneous crystal of SAPO-5 molecular sieves was inhibited, pure SAPO-34 molecular sieve was obtained, and a crystallization period shortened by 24 h. But when amount of crystal seed reached a certain limit,the raising of crystallinity of SAPO-34 smoothed out.