锂离子电池%正极材料%混合正极%LiFePO_4%LiMn_2O_4
鋰離子電池%正極材料%混閤正極%LiFePO_4%LiMn_2O_4
리리자전지%정겁재료%혼합정겁%LiFePO_4%LiMn_2O_4
Li-ion battery%cathode material%mixed cathode%LiFePO_4%LiMn_2O_4
将LiFePO_4和LiMn_2O_4按78:9的质量比混合,并用作锂离子电池正极材料.使用该混合正极的14500型电池适宜的充放电电压范围为4.20~2.50 V,在常温下以1.0 C循环250次,容量保持率为87.47%;在60 ℃下以1.0 C循环12次,容量保持率为84.62%.电池以100%SOC在60 ℃下贮存7 d后,容量保持率为82.50%,容量恢复率为89.01%.
將LiFePO_4和LiMn_2O_4按78:9的質量比混閤,併用作鋰離子電池正極材料.使用該混閤正極的14500型電池適宜的充放電電壓範圍為4.20~2.50 V,在常溫下以1.0 C循環250次,容量保持率為87.47%;在60 ℃下以1.0 C循環12次,容量保持率為84.62%.電池以100%SOC在60 ℃下貯存7 d後,容量保持率為82.50%,容量恢複率為89.01%.
장LiFePO_4화LiMn_2O_4안78:9적질량비혼합,병용작리리자전지정겁재료.사용해혼합정겁적14500형전지괄의적충방전전압범위위4.20~2.50 V,재상온하이1.0 C순배250차,용량보지솔위87.47%;재60 ℃하이1.0 C순배12차,용량보지솔위84.62%.전지이100%SOC재60 ℃하저존7 d후,용량보지솔위82.50%,용량회복솔위89.01%.
LiFePO_4 and LiMn_2O_4 was mixed with the mass ratio of 78:9 and used as cathode material of Li-ion battery. The pro-per charge-discharge voltage range of 14500 type battery using the mixed cathode was 4.20~2.50 V. When 1.0 C cycle at room temperature,the capacity retention rate was 87.47% after 250 cycles,when 1.0 C cycle at 60 ℃,the capacity retention rate was 84.62% after 12 cycles. When the battery was stored 7 d at 60 ℃ with 100% SOC,the capacity retention rate was 82.50%,the capacity recovery rate was 89.01%.