TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA
2002年
4期
676-680
,共5页
E.Strom%张继%冯荻
E.Strom%張繼%馮荻
E.Strom%장계%풍적
indentation toughness%Mo5Si3%alloying
The indentation toughness of Mo5Si3 -based phases was studied with regard to different alloying elements, amount of alloying addition as well as the presence of secondary phases. Cr, Ti, Nb, Ni and Co were added as alloying elements. The results show that the indentation fracture toughness of Mo5Si3 increases with the alloying additions, from 2.4 Mpa *m1/2 for mon olithic to just over 3 Mpa*m1/2 for highly alloyed Mo5Si3. Small volume fractions of brittle secondary phases may have a positive impact on the inde ntation toughness; while larger fractions seems to lower the toughness.