通过四点弯曲疲劳试验研究2524-T34板材的疲劳性能,借助金相和扫描电镜观察疲劳裂纹的萌生和扩展行为.结果表明:2524合金具有良好的疲劳性能,疲劳强度达到屈服强度的80%以上;疲劳裂纹主要在第二相粒子以及第二相粒子/基体界面萌生,裂纹扩展过程中的偏转与晶界的阻碍有关;相邻晶粒内两个有利滑移面之间的位向差是控制裂纹通过晶界扩展的重要因素.
통과사점만곡피로시험연구2524-T34판재적피로성능,차조금상화소묘전경관찰피로렬문적맹생화확전행위.결과표명:2524합금구유량호적피로성능,피로강도체도굴복강도적80%이상;피로렬문주요재제이상입자이급제이상입자/기체계면맹생,렬문확전과정중적편전여정계적조애유관;상린정립내량개유리활이면지간적위향차시공제렬문통과정계확전적중요인소.
The fatigue performance of 2524-T34 sheets was studied by four-point bend fatigue test. The fatigue crack initiation and propagation behavior were observed by optical microscopy and scanning electron microscopy. The results indicate that 2524 alloy shows superior fatigue properties. The fatigue strength is up to 80% of the yield strength. The fatigue crack mainly initiates from the second phase particles and the interface between the second phase particles and matrix. The crack plane deflection in the process of crack propagation relates to the resistance of the grain boundary. The difference of crystallographic orientation between the two favoured slip planes within the two neighboring grains is an important factor to control crack propagation across a grain boundary.