采用标准固相反应法制备了La0.45Ca0.55Mn1-xO3(x=0.00,0.06,0.10,0.12)多晶样品.通过XRD、ρ-T曲线、M-T曲线和ρ-T拟合曲线,研究了Mn位V5+离子掺杂对体系的电荷有序相及输运性质的影响.实验结果表明:随着V5+离子的掺杂量的增加,电荷有序相(CO)逐渐削弱,当x=0.10时,CO相基本融化但还有部分残留,当x=0.12时CO相完全融化;对低掺杂(x=0.00,0.06)样品,表现出复杂磁相:随温度降低,发生顺磁-电荷有序-反铁磁相变,40 K附近,在反铁磁背景下产生再入型自旋玻璃态;随掺杂量增加,体系的电阻率逐渐减小,当掺杂量x≥0.10时,样品发生金属-绝缘体相变,其相变温度随着掺杂量的增加而向高温移动.对于金属型导电机制满足自旋波散射和电-磁子之间的散射,而绝缘体导电机制有两种情况:x≤0.10的样品满足变程跃迁模型ρ=ρ0exp(T0/T) 1/4,x=0.12的样品则满足小极化子绝热最近邻跃迁模型ρ=ATexp(Eα/κBT),通过掺杂实现了从变程跃迁到绝热小极化子最近邻跃迁.
채용표준고상반응법제비료La0.45Ca0.55Mn1-xO3(x=0.00,0.06,0.10,0.12)다정양품.통과XRD、ρ-T곡선、M-T곡선화ρ-T의합곡선,연구료Mn위V5+리자참잡대체계적전하유서상급수운성질적영향.실험결과표명:수착V5+리자적참잡량적증가,전하유서상(CO)축점삭약,당x=0.10시,CO상기본융화단환유부분잔류,당x=0.12시CO상완전융화;대저참잡(x=0.00,0.06)양품,표현출복잡자상:수온도강저,발생순자-전하유서-반철자상변,40 K부근,재반철자배경하산생재입형자선파리태;수참잡량증가,체계적전조솔축점감소,당참잡량x≥0.10시,양품발생금속-절연체상변,기상변온도수착참잡량적증가이향고온이동.대우금속형도전궤제만족자선파산사화전-자자지간적산사,이절연체도전궤제유량충정황:x≤0.10적양품만족변정약천모형ρ=ρ0exp(T0/T) 1/4,x=0.12적양품칙만족소겁화자절열최근린약천모형ρ=ATexp(Eα/κBT),통과참잡실현료종변정약천도절열소겁화자최근린약천.