中国有色金属学报(英文版)
中國有色金屬學報(英文版)
중국유색금속학보(영문판)
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA
2011年
6期
1428-1434
,共7页
张青青%苏耿%李傲生%刘开宇
張青青%囌耿%李傲生%劉開宇
장청청%소경%리오생%류개우
Co3O4%储氢合金%容量%电化学性能
Co3O4%儲氫閤金%容量%電化學性能
Co3O4%저경합금%용량%전화학성능
Co3O4%hydrogen storage alloy%capacity%electrochemical performance
将不同含量的Co3O4(2%,4%,6%,8%,质量分数)作为添加剂加入到储氢合金中,采用机械混合法进行改性处理.对添加Co3O4的合金电极的电化学性能和电极过程进行研究.结果表明:放电容量有了较大增加,添加2%、4%、6%、8% Co3O4的电极放电容量比空白电极容量分别增加0.83%,4.86%,7.18%和9.21%.线性极化曲线和电化学阻抗谱测试表明,添加Co3O4降低了电极的电荷转移电阻.循环伏安、扫描电镜和EDS测试表明,添加的Co3O4可部分溶解,发生Co-Co(OH)2可逆氧化一还原反应,从而改善储氢合金的电化学性能.
將不同含量的Co3O4(2%,4%,6%,8%,質量分數)作為添加劑加入到儲氫閤金中,採用機械混閤法進行改性處理.對添加Co3O4的閤金電極的電化學性能和電極過程進行研究.結果錶明:放電容量有瞭較大增加,添加2%、4%、6%、8% Co3O4的電極放電容量比空白電極容量分彆增加0.83%,4.86%,7.18%和9.21%.線性極化麯線和電化學阻抗譜測試錶明,添加Co3O4降低瞭電極的電荷轉移電阻.循環伏安、掃描電鏡和EDS測試錶明,添加的Co3O4可部分溶解,髮生Co-Co(OH)2可逆氧化一還原反應,從而改善儲氫閤金的電化學性能.
장불동함량적Co3O4(2%,4%,6%,8%,질량분수)작위첨가제가입도저경합금중,채용궤계혼합법진행개성처리.대첨가Co3O4적합금전겁적전화학성능화전겁과정진행연구.결과표명:방전용량유료교대증가,첨가2%、4%、6%、8% Co3O4적전겁방전용량비공백전겁용량분별증가0.83%,4.86%,7.18%화9.21%.선성겁화곡선화전화학조항보측시표명,첨가Co3O4강저료전겁적전하전이전조.순배복안、소묘전경화EDS측시표명,첨가적Co3O4가부분용해,발생Co-Co(OH)2가역양화일환원반응,종이개선저경합금적전화학성능.
Anodic electrodes with the mixture of hydrogen storage alloys and different contents of Co3O4 (2%,4%,6% and 8%,mass fraction) powders were made.The effects of Co3O4 on the electrochemical performance of the alloy electrodes were studied.The constant charge-discharge tests show that the discharge capacity of alloy electrodes with Co3O4 significantly increases,and the maximum discharge capacities of electrodes with 2%,4%,6% and 8% Co3O4 are higher than the electrode with no Co3O4 by 0.83%,4.86%,7.18% and 9.21%,accordingly.Linear polarization (LP) and electrochemical impedance spectroscopy (EIS) tests suggest that charge-transfer resistance decreases by the addition of Co3O4.Cyclic voltammogram (CV),scanning electron microscopy (SEM) and energy dispersive spectrum (EDS) tests indicate that Co3O4 can partly dissolve and experience a reversible oxidation-reduction process of Co to Co (OH)2,leading to the improvement in the electrochemical performance of hydrogen storage alloy.