JOURNAL OF FUNCTIONAL MATERIALS
2009年
12期
2077-2080
,共4页
刘强%何捷%蒋波%郑丹%万渝平%孙鹏%林理彬
劉彊%何捷%蔣波%鄭丹%萬渝平%孫鵬%林理彬
류강%하첩%장파%정단%만투평%손붕%림리빈
辐射变色薄膜%紫外辐照%能量密度%响应吸光度%剂量计
輻射變色薄膜%紫外輻照%能量密度%響應吸光度%劑量計
복사변색박막%자외복조%능량밀도%향응흡광도%제량계
radiochromic film%ultraviolet radiation irradiation%energy density%absorbency response%dosimeter
以聚乙烯醇缩丁醛(PVB)为基质,以高敏性类丁二炔化合物为主要有机染色材料,添加适当比例光引发剂,成功研制了一种高感度新型辐射变色膜.用CL-1000型紫外线交联仪进行紫外线辐照后,薄膜颜色由粉红渐变为蓝色,且随着辐照剂量的增加颜色深度递增.经分光光度计测试其吸收光谱,发现主吸收峰值出现在650nm附近,且在相同的紫外线能量密度下,吸收峰处的响应吸光度与辐照时间成线性响应关系.在相同的辐照时间内,吸收峰处的响应吸光度与紫外线能量密度亦成线性关系.染色材料中添加适当比例的光引发剂,可以提高薄膜的响应吸光度,进而提高其响应灵敏度.对于变色层厚度为30~60μm的辐射变色膜,敏感层厚度与吸光度响应成正相关性.室温下避光贮存60天内,此新型辐射变色膜具有较好的稳定性与可重复性.
以聚乙烯醇縮丁醛(PVB)為基質,以高敏性類丁二炔化閤物為主要有機染色材料,添加適噹比例光引髮劑,成功研製瞭一種高感度新型輻射變色膜.用CL-1000型紫外線交聯儀進行紫外線輻照後,薄膜顏色由粉紅漸變為藍色,且隨著輻照劑量的增加顏色深度遞增.經分光光度計測試其吸收光譜,髮現主吸收峰值齣現在650nm附近,且在相同的紫外線能量密度下,吸收峰處的響應吸光度與輻照時間成線性響應關繫.在相同的輻照時間內,吸收峰處的響應吸光度與紫外線能量密度亦成線性關繫.染色材料中添加適噹比例的光引髮劑,可以提高薄膜的響應吸光度,進而提高其響應靈敏度.對于變色層厚度為30~60μm的輻射變色膜,敏感層厚度與吸光度響應成正相關性.室溫下避光貯存60天內,此新型輻射變色膜具有較好的穩定性與可重複性.
이취을희순축정철(PVB)위기질,이고민성류정이결화합물위주요유궤염색재료,첨가괄당비례광인발제,성공연제료일충고감도신형복사변색막.용CL-1000형자외선교련의진행자외선복조후,박막안색유분홍점변위람색,차수착복조제량적증가안색심도체증.경분광광도계측시기흡수광보,발현주흡수봉치출현재650nm부근,차재상동적자외선능량밀도하,흡수봉처적향응흡광도여복조시간성선성향응관계.재상동적복조시간내,흡수봉처적향응흡광도여자외선능량밀도역성선성관계.염색재료중첨가괄당비례적광인발제,가이제고박막적향응흡광도,진이제고기향응령민도.대우변색층후도위30~60μm적복사변색막,민감층후도여흡광도향응성정상관성.실온하피광저존60천내,차신형복사변색막구유교호적은정성여가중복성.
A new high sensitive radiochromic film is developed by using poly(vinyl butyral) as the base and using acetylene-type compounds as organic dye material, it becomes blue after irradiated by low energy density of ultraviolet radiation using CL-100 UV cross-linking instrument, then, analyzed by absorb spectrum, the absorption peak in visual region locates about 650nm. There is a linear relationship between absorbency and the irradiation time of ultraviolet radiation when irradiated by the same energy density. A linear relationship between absorbency and energy density in the absorption peak also be discovered. Fitting a linear relationship between the thickness and absorbency.The sensitivity of the response can be changed when different inverse proportion of halides are added into the radiochromic system. Good stability is proved from experimental analysis in 60 days.