中温固体氧化物燃料电池%阳极负载%多层电解质
中溫固體氧化物燃料電池%暘極負載%多層電解質
중온고체양화물연료전지%양겁부재%다층전해질
采用柠檬酸法合成了Gd0.1Ce0.9O1.95(GDC)、La0.45Ce0.55O2-α/2(LDC)、La0.9Sr0.1Ga0.8Mg0.2O2.85(LSGM)电解质材料,并制备了阳极负载型GDC-LSGM、LDC-LSGM和LDC-LSGM-LDC多层薄膜电解质单体电池,考察了单体电池的U-J特性和功率输出性能.结果显示:GDC-LSGM电解质电池没有电流产生;LDC-LSGM电解质电池最大输出功率密度最高,800℃时约为0.72W/cm2,但不稳定;LDC-LSGM-LDC多层电解质电池的开路电压最高,800℃时可达0.814 V.
採用檸檬痠法閤成瞭Gd0.1Ce0.9O1.95(GDC)、La0.45Ce0.55O2-α/2(LDC)、La0.9Sr0.1Ga0.8Mg0.2O2.85(LSGM)電解質材料,併製備瞭暘極負載型GDC-LSGM、LDC-LSGM和LDC-LSGM-LDC多層薄膜電解質單體電池,攷察瞭單體電池的U-J特性和功率輸齣性能.結果顯示:GDC-LSGM電解質電池沒有電流產生;LDC-LSGM電解質電池最大輸齣功率密度最高,800℃時約為0.72W/cm2,但不穩定;LDC-LSGM-LDC多層電解質電池的開路電壓最高,800℃時可達0.814 V.