热加工工艺
熱加工工藝
열가공공예
HOT WORKING TECHNOLOGY
2010年
8期
36-37,41
,共3页
魏谨凭%卫广智%时雨%杨金尧
魏謹憑%衛廣智%時雨%楊金堯
위근빙%위엄지%시우%양금요
SWRH82B%晶粒度%金相组织%屈服强度%再结晶
SWRH82B%晶粒度%金相組織%屈服彊度%再結晶
SWRH82B%정립도%금상조직%굴복강도%재결정
SWRH82B%grain size%microstructure%yiled strength%re-erystallization
研究了SWRH82B钢在高温多道次高变形速率下再结晶的规律.结果表明,随轧制道次的增加,晶粒尺寸逐渐减小,索氏体的含量不断增加,屈服强度逐渐提高.
研究瞭SWRH82B鋼在高溫多道次高變形速率下再結晶的規律.結果錶明,隨軋製道次的增加,晶粒呎吋逐漸減小,索氏體的含量不斷增加,屈服彊度逐漸提高.
연구료SWRH82B강재고온다도차고변형속솔하재결정적규률.결과표명,수알제도차적증가,정립척촌축점감소,색씨체적함량불단증가,굴복강도축점제고.
The re-crystallization rule of SWRH82B steel at high-temperature,more rolling times and high deformation rate was studied.The results indicate that,with the increase of rolling times,the grain size becomes smaller,the content of sorbite multiplieates,and the yield strength improves.