基于轧制态Ni-5％W(原子分数)合金基带短样品在不同温度退火的结果,对Ni-5％W合金长带进行了辊到辊退火处理.分析不同温度下退火后的硬度,通过X射线极图法评价再结晶织构,采用光学显微镜分析基带的微观结构,讨论退火温度对再结晶织构的影响,考察短带与长带再结晶织构的差异.结果发现:长带和短带都具有很强的立方织构.
기우알제태Ni-5％W(원자분수)합금기대단양품재불동온도퇴화적결과,대Ni-5％W합금장대진행료곤도곤퇴화처리.분석불동온도하퇴화후적경도,통과X사선겁도법평개재결정직구,채용광학현미경분석기대적미관결구,토론퇴화온도대재결정직구적영향,고찰단대여장대재결정직구적차이.결과발현:장대화단대도구유흔강적립방직구.
Cold rolled Ni-5at％W substrates with short length were annealed at different temperatures.On the basis of the results of annealing of short length substrates,the substrates with long length were annealed by reel-to-reel method.The hardness of the annealed substrates at different temperatures was analyzed.The recrystallization textures were evaluated by X-ray pole figure and the microstructure were investigated by optical microscopy.The effects of annealing temperature on the recrystalization texture were discussed.The differences of recrystallization texture between short length substrates and long length substrates were investigated.It is found that both short length substrates and long length substrates have very strong cube texture.