U71Mn rail%flash welding%induction normalizing%flame normalizing
通过对U71Mn闪光焊经火焰正火和感应正火处理后的接头进行拉伸、冲击及硬度试验,对比两种正火方式对上述性能的影响.研究认为感应正火更有利于提高U71Mn钢轨闪光焊焊后接头性能.
通過對U71Mn閃光銲經火燄正火和感應正火處理後的接頭進行拉伸、遲擊及硬度試驗,對比兩種正火方式對上述性能的影響.研究認為感應正火更有利于提高U71Mn鋼軌閃光銲銲後接頭性能.
통과대U71Mn섬광한경화염정화화감응정화처리후적접두진행랍신、충격급경도시험,대비량충정화방식대상술성능적영향.연구인위감응정화경유리우제고U71Mn강궤섬광한한후접두성능.
The effects of normalizing way on the mechanical properties of U71Mn rail joint after flash welding were studied through tension, impact and hardness test. The results show that induction normalizing have more help to improve the property of weld joints than flame normalizing.