研究了不同冷却速度下CuCr25合金的微观组织和凝固过程.随着冷却速度的增加,CuCr25合金的微观组织将变得越来越细.当冷却速度达到107K/s时,可获得纳米结构的微观组织.当冷却速度＜103K/s时,CuCr25合金的凝固过程为普通凝固过程;如果冷却速度＞104K/s,其凝固过程为液相分解凝固过程.在快速凝固过程中,CuCr25合金中没有新相形成.但是,Cu在富Cr相中和Cr在富Cu相中的溶解度有所增加.
연구료불동냉각속도하CuCr25합금적미관조직화응고과정.수착냉각속도적증가,CuCr25합금적미관조직장변득월래월세.당냉각속도체도107K/s시,가획득납미결구적미관조직.당냉각속도＜103K/s시,CuCr25합금적응고과정위보통응고과정;여과냉각속도＞104K/s,기응고과정위액상분해응고과정.재쾌속응고과정중,CuCr25합금중몰유신상형성.단시,Cu재부Cr상중화Cr재부Cu상중적용해도유소증가.
The microstructures and solidification processes of CuCr25 alloys are studied under different cooling rates in the present paper. With increasing of the cooling rate, the microstructures of CuCr25 alloys become finer and finer. When the cooling rate is up to 107K/s, nano-microstructures can be obtained. When the cooling rate is ＜103K/s, the solidification process of CuCr25 alloys belongs to a general solidification process; if the cooling rate is ＞104K/s, it belongs to the liquid phase separation process. In rapid solidification process, there is no new phase formed in CuCr25 alloys, but the solubility of Cu in Cr-rich phase and Cr in Cu-rich phase will increase.