JOURNAL OF CHINESE LACQUER
2011年
4期
1-3,43
,共4页
漆酚%氯化铁%紫外光固化%抗紫外性能
漆酚%氯化鐵%紫外光固化%抗紫外性能
칠분%록화철%자외광고화%항자외성능
Urushiol%FeC13%UV curing%Anti - ultraviolet
通过紫外光固化法快速便捷地由漆酚和三氯化铁制备了色泽乌黑、表面平整光亮的漆酚铁聚合物。当漆酚和氯化铁的物质的量比为3:1,紫外光辐照20s时,漆膜具有优良的常规物理机械性能:光泽度132%,硬度6H,冲击强度50kg.cm,柔韧性0.5mm,附着力1级;良好的抗紫外线性能:紫外光辐照1200h以后,其失光率仅为4.85%;良好的耐热性能:受热320℃时失重5%;优异的抗化学介质性能。
通過紫外光固化法快速便捷地由漆酚和三氯化鐵製備瞭色澤烏黑、錶麵平整光亮的漆酚鐵聚閤物。噹漆酚和氯化鐵的物質的量比為3:1,紫外光輻照20s時,漆膜具有優良的常規物理機械性能:光澤度132%,硬度6H,遲擊彊度50kg.cm,柔韌性0.5mm,附著力1級;良好的抗紫外線性能:紫外光輻照1200h以後,其失光率僅為4.85%;良好的耐熱性能:受熱320℃時失重5%;優異的抗化學介質性能。
통과자외광고화법쾌속편첩지유칠분화삼록화철제비료색택오흑、표면평정광량적칠분철취합물。당칠분화록화철적물질적량비위3:1,자외광복조20s시,칠막구유우량적상규물리궤계성능:광택도132%,경도6H,충격강도50kg.cm,유인성0.5mm,부착력1급;량호적항자외선성능:자외광복조1200h이후,기실광솔부위4.85%;량호적내열성능:수열320℃시실중5%;우이적항화학개질성능。
By UV irradiation, the urushiol - iron polymer films with black mirrored surface were prepared quickly from urushiol and FeC13. When the molar ratio of urushiol and FeCl3 was 3:1 and the time of UV irradiation was 20s, the obtained film exhibited good physieo - mechanical properties : the gloss 132% , the hardness 6H, the impact strength 50kg. cm, the flexibility 0. 5mm, and the adhesion 1 degree. Moreover, the film had good ultraviolet resistance with the gloss loss rate of 4.85% after 1200h antiuhraviolet test, and good thermal stability and anticorrosive properties.