张智强%胡向博%李凌峰%霍世超
張智彊%鬍嚮博%李凌峰%霍世超
장지강%호향박%리릉봉%곽세초
聚羧酸系减水剂%氧化还原引发体系%水泥净浆流动度
聚羧痠繫減水劑%氧化還原引髮體繫%水泥淨漿流動度
취최산계감수제%양화환원인발체계%수니정장류동도
polycarboxylate superplasticizer%redox system%cement paste fluidity
采用自制的聚乙二醇单甲醚1500甲基丙烯酸酯(MPEG1500-MAA)和甲基丙烯酸(MAA)试剂,在不同引发体系下合成聚羧酸系高效减水剂。分别探讨了甲基丙烯磺酸钠(SMAS)、甲基丙烯酸(MAA)以及引发剂过硫酸铵(PASM)的掺量与减水剂分散性和分散保持性的关系,研究了过硫酸铵—亚硫酸氢钠、过硫酸铵—亚硫酸氢钠—亚铁盐和过氧化氢—亚硫酸氢钠—亚铁盐三种氧化还原引发体系中各组分掺量、反应温度对减水剂分散性及分散保持性的影响,确定了在氧化还原引发体系条件下,减水剂反应温度可降低到60℃左右,所合成的减水剂为水泥折固掺量0.3%,水灰比为0.29时,其净浆流动度达250~260mm,30min流动度保持率大于95%。
採用自製的聚乙二醇單甲醚1500甲基丙烯痠酯(MPEG1500-MAA)和甲基丙烯痠(MAA)試劑,在不同引髮體繫下閤成聚羧痠繫高效減水劑。分彆探討瞭甲基丙烯磺痠鈉(SMAS)、甲基丙烯痠(MAA)以及引髮劑過硫痠銨(PASM)的摻量與減水劑分散性和分散保持性的關繫,研究瞭過硫痠銨—亞硫痠氫鈉、過硫痠銨—亞硫痠氫鈉—亞鐵鹽和過氧化氫—亞硫痠氫鈉—亞鐵鹽三種氧化還原引髮體繫中各組分摻量、反應溫度對減水劑分散性及分散保持性的影響,確定瞭在氧化還原引髮體繫條件下,減水劑反應溫度可降低到60℃左右,所閤成的減水劑為水泥摺固摻量0.3%,水灰比為0.29時,其淨漿流動度達250~260mm,30min流動度保持率大于95%。
채용자제적취을이순단갑미1500갑기병희산지(MPEG1500-MAA)화갑기병희산(MAA)시제,재불동인발체계하합성취최산계고효감수제。분별탐토료갑기병희광산납(SMAS)、갑기병희산(MAA)이급인발제과류산안(PASM)적참량여감수제분산성화분산보지성적관계,연구료과류산안—아류산경납、과류산안—아류산경납—아철염화과양화경—아류산경납—아철염삼충양화환원인발체계중각조분참량、반응온도대감수제분산성급분산보지성적영향,학정료재양화환원인발체계조건하,감수제반응온도가강저도60℃좌우,소합성적감수제위수니절고참량0.3%,수회비위0.29시,기정장류동도체250~260mm,30min류동도보지솔대우95%。
Polycarboxylic acid superplasticizer was synthesized at different initiator system by using the meacrylic acid(AR)and the meacrylic acid and the polyethylene glycol single methyl ether(1500)(MPEG1500-MAA)(homemade).Relationship is discussed respectively between dosage of methyl propene sulfonate(SMAS),methacrylic acid(MAA)and initiator ammonium persulfate(PASM)and dispersion and dispersed retention of polycarboxylic acid superplasticizer.Based on the above results,Relationship is studied respectively between the dosage of ammonium persulfate-sodium bisulfite,ammonium persulfate-sodium bisulfite-ferrous salt,hydrogen peroxidesodium bisulfite-ferrous salt and reaction temperature and dispersion and dispersed retention of polycarboxylic acid superplasticizer.Under the conditions of the redox system,temperature can be reduced to 60℃,with addition of 0.3%neat copolymer and water-cement ratio of 0.29,paste fluidity is in the 250-260mm,fluidity retention rate is more than95%.