In the present study, rapidly solidified ribbons of Al87 Ni7Cu3 Nd3 metallic glass was prepared by usingmelt spinning. Devitrification process of the totally amorphous ribbons was investigated by high temperature X-raydiffraction analysis, combining with differential scanning calorimetry, under continuous and isothermal heating re-gime. The X-ray diffraction intensity and full width at the half maximum (FWHM) were analyzed to investigate theincrease of crystallized amount and growth of α-Al crystal particles. The results show that under continuous heatingregime, the metallic glass devitrifies via two main stages: primary crystallization, resulting in two-phase mixture ofα-Al plus residual amorphous phase, and secondary crystallization, corresponding to rapid precipitation of some in-ter-metallic phases in the form of dispersion or eutectic mixture. Under isothermal heating regime, only Al crystalprecipitates from the Al-rich amorphous matrix at low temperature, and when heating at 280 ℃ only Al crystal pre-cipitates within a short time, and then Al8 Cu4 Nd forms, followed by Al3 Ni, in the residual amorphous phase. Whenheating at higher temperature or for longer time, Aln Nd3 forms, the amorphous phase disappears, and the ribbonsdevelop into polycrystalline morphologies with multiply phase mixture of a-Al, Al8 Cu4 Nd, Al3 Ni, and Al11 Nd3.