为了改善记录介质的磁性能,研究了溅射Cr和CrTi底层对Co68Cr17Pt15性能的影响.发现在玻璃盘基和CoCrPt磁性层之间引入100 nm厚的Cr底层,可使介质矫顽力从56 kA·m-1增加到127 kA·m-1,同时剩磁比和矫顽力矩形比分别增加66%和74%.同时还发现Cr底层厚度对介质磁性能有较大影响.考虑到减小Cr底层和磁性层的晶格匹配,在Cr底层里添加Ti元素,当Ti原子分数达到1.5%时,即使在室温下溅射,薄膜也有好的面内磁滞回线,此时矫顽力可达到160 kA·m-1.X射线衍射表明在介质中引入Cr和CrTi底层,由于薄膜能更好的沿着垂直于易磁化轴方向生长而使介质性能提高.
위료개선기록개질적자성능,연구료천사Cr화CrTi저층대Co68Cr17Pt15성능적영향.발현재파리반기화CoCrPt자성층지간인입100 nm후적Cr저층,가사개질교완력종56 kA·m-1증가도127 kA·m-1,동시잉자비화교완력구형비분별증가66%화74%.동시환발현Cr저층후도대개질자성능유교대영향.고필도감소Cr저층화자성층적정격필배,재Cr저층리첨가Ti원소,당Ti원자분수체도1.5%시,즉사재실온하천사,박막야유호적면내자체회선,차시교완력가체도160 kA·m-1.X사선연사표명재개질중인입Cr화CrTi저층,유우박막능경호적연착수직우역자화축방향생장이사개질성능제고.
The effect of sputtering Cr or CrTi underlayers on the performances of Co68Cr17Pt15 thin films were studied to nm-thick Cr underlayer between the CoCrPt magnetic layer and glass substrate, and that the Cr underlayer thickness has greater effect on the magnetic properties. In order to reduce the lattice mismatch between the Cr underlayer and the magnetic layer, the Cr underlayer was doped with Ti element. When Ti content is 15 at%, the film has square in-plane loop and the show that the enhancement of coercivity and improvement of S and S* should be attributed to the favorable film growth along the orientation perpendicular to the magnetization axis by introducing Cr or CrTi underlayer in the media.