废胶粉%共轭三组分%互穿聚合物网络
廢膠粉%共軛三組分%互穿聚閤物網絡
폐효분%공액삼조분%호천취합물망락
scrap rubber powder%conjugated three-component%interpenetrating polymer networks
对废胶粉进行了裂解气相色谱、红外光谱、热重分析,并且制备了共轭三组分聚氨酯/聚苯乙烯,废胶粉半互穿聚合物网络(PU/PS/SRP-IPN),并进行了力学性能测试.结果表明:在废胶粉中含有天然橡胶、顺丁橡胶、丁苯橡胶,其中天然橡胶含量较高,顺丁橡胶和丁苯橡胶含量较低,三种胶的含量比为天然橡胶:顺丁橡胶:丁苯橡胶为12:6.2:1;胶粉含胶率为49.61%,炭黑含量为18.89%,无机填料含量为21.01%.当聚苯乙烯含量为40%时,体系的扯断伸长率与拉伸强度都出现最大值,随着聚苯乙烯在体系中所占比例增大,硬度与永久变形逐渐增大.差示扫描量热仪测定的玻璃化转变温度和扫描电镜分析结果表明作为公共组分的聚苯乙烯与废胶粉及聚氨酯发生了互穿缠结,整个材料性能得以提高.
對廢膠粉進行瞭裂解氣相色譜、紅外光譜、熱重分析,併且製備瞭共軛三組分聚氨酯/聚苯乙烯,廢膠粉半互穿聚閤物網絡(PU/PS/SRP-IPN),併進行瞭力學性能測試.結果錶明:在廢膠粉中含有天然橡膠、順丁橡膠、丁苯橡膠,其中天然橡膠含量較高,順丁橡膠和丁苯橡膠含量較低,三種膠的含量比為天然橡膠:順丁橡膠:丁苯橡膠為12:6.2:1;膠粉含膠率為49.61%,炭黑含量為18.89%,無機填料含量為21.01%.噹聚苯乙烯含量為40%時,體繫的扯斷伸長率與拉伸彊度都齣現最大值,隨著聚苯乙烯在體繫中所佔比例增大,硬度與永久變形逐漸增大.差示掃描量熱儀測定的玻璃化轉變溫度和掃描電鏡分析結果錶明作為公共組分的聚苯乙烯與廢膠粉及聚氨酯髮生瞭互穿纏結,整箇材料性能得以提高.
대폐효분진행료렬해기상색보、홍외광보、열중분석,병차제비료공액삼조분취안지/취분을희,폐효분반호천취합물망락(PU/PS/SRP-IPN),병진행료역학성능측시.결과표명:재폐효분중함유천연상효、순정상효、정분상효,기중천연상효함량교고,순정상효화정분상효함량교저,삼충효적함량비위천연상효:순정상효:정분상효위12:6.2:1;효분함효솔위49.61%,탄흑함량위18.89%,무궤전료함량위21.01%.당취분을희함량위40%시,체계적차단신장솔여랍신강도도출현최대치,수착취분을희재체계중소점비례증대,경도여영구변형축점증대.차시소묘량열의측정적파리화전변온도화소묘전경분석결과표명작위공공조분적취분을희여폐효분급취안지발생료호천전결,정개재료성능득이제고.
The pyrolytic gas chromatography, Fourier transform infrared spectrometry and thermogravimetric analysis were carried on to determine the ingredient of scrap robber powder, and the conjugated three-component polyurethane/polystyrene /scrap rubber powder semi-interpenetrating polymer networks was prepared to test the mechnical performance. Results indicated that the natural rubber, the butadiene rubber and the styrene butadiene rubber were contained in the scrap rubber powder, which the content of the natural rubber was richer than that of the butadiene rubber and the styrene butadiene rubber with three kind of rubber content ratio being natural rubber:butadiene rubber:butadiene styrene rubber of 12:6.2:1. The rubber contained in the scrap rubber powder was 49.61%, the carbon black being 18.89%, the inorganic padding being 21.01%. The tensile strength and the elongation at break appeared the maximum value with the PS content 40%, the permanent set and the hardness were enlarged gradually along with the PS proportion in the system increasing. The vitrification transition temperature decided by differential scanning calorimetry and the scanning electron microscope analysis indicated that the polystyrene,which occurred as public component, interpenetrated with polyurethane and scrap rubber'powder, which improved the property of whole material.