尼龙合金%马来酸酐%相容剂%SEBS
尼龍閤金%馬來痠酐%相容劑%SEBS
니룡합금%마래산항%상용제%SEBS
nylon alloy%maleic anhydride%compatibilizer%SEBS (styrene-b-(ethylene-co-butylenes)-b-styrene triblock copolymer)
利用红外光谱测定了接枝样品,用其中马来酸酐(MAH)的特征峰与苯乙烯/乙烯/丁烯/苯乙烯嵌段共聚物(SEBS)的特征峰之比值来表达接枝率,探索了接枝时MAH和助剂的量对接枝率的影响,同时探讨了不同接枝率的相容剂及不同比值的聚苯醚(PPO)/尼龙6(PA6)对PPO/PA6合金的增容作用及其对合金的综合性能影响.结果表明:(1)加入合适的助剂有利于SEBS体系的接枝,而当MAH的加入量为3%时得到的接枝率最高;(2)接枝率提高,合金的综合性能稍有改善;(3)PPO/PA6 = 70/30时性能指标达到最优.而接枝的SEBS加入量10%时PPO/PA6合金的综合性能最优.
利用紅外光譜測定瞭接枝樣品,用其中馬來痠酐(MAH)的特徵峰與苯乙烯/乙烯/丁烯/苯乙烯嵌段共聚物(SEBS)的特徵峰之比值來錶達接枝率,探索瞭接枝時MAH和助劑的量對接枝率的影響,同時探討瞭不同接枝率的相容劑及不同比值的聚苯醚(PPO)/尼龍6(PA6)對PPO/PA6閤金的增容作用及其對閤金的綜閤性能影響.結果錶明:(1)加入閤適的助劑有利于SEBS體繫的接枝,而噹MAH的加入量為3%時得到的接枝率最高;(2)接枝率提高,閤金的綜閤性能稍有改善;(3)PPO/PA6 = 70/30時性能指標達到最優.而接枝的SEBS加入量10%時PPO/PA6閤金的綜閤性能最優.
이용홍외광보측정료접지양품,용기중마래산항(MAH)적특정봉여분을희/을희/정희/분을희감단공취물(SEBS)적특정봉지비치래표체접지솔,탐색료접지시MAH화조제적량대접지솔적영향,동시탐토료불동접지솔적상용제급불동비치적취분미(PPO)/니룡6(PA6)대PPO/PA6합금적증용작용급기대합금적종합성능영향.결과표명:(1)가입합괄적조제유리우SEBS체계적접지,이당MAH적가입량위3%시득도적접지솔최고;(2)접지솔제고,합금적종합성능초유개선;(3)PPO/PA6 = 70/30시성능지표체도최우.이접지적SEBS가입량10%시PPO/PA6합금적종합성능최우.
In this paper, samples of SEBS melt grafted with maleic anhydride (MAH) were inspected by using IR spectroscopy, and the graft ratio was expressed as the ratio between the area of IR characteristic peak of MAH and that of SEBS. The influences of the added amount of MAH and adding promoter on the graft ratio were investigated. Moreover, the effects of SEBS-g-MAH with different graft ratios and the different proportions of PPO to Nylon-6 on the properties of PPO/PA6 alloy were studied. The results show that: (1) adding appropriate promoter can favor the graft polymerization, and the highest graft ratio can be obtained when the used amount of MAH is 3%;(2) the overall properties of the prepared PPO/PA6 alloy can be somewhat improved by using SEBS-g-MAH with higher graft ratio;(3) the prepared alloy having optimal property can be obtained when the proportion of PPO to Nylon-6 is 70:30 and the used amount of grafted SEBS is 10%.