CAJ | 학술논문

采用放电等离子烧结技术(SPS)制备P型复相Ga2Te5基化合物,对其进行微观分析和热电性能测试.通过XRD分析观察到主相Ga2Te5和少量的SnTe、单质Te.在整个测试温度(319～549 K)范围内,Ga2Te5基化合物的Seebeck系数、电导率和热导率都随温度的升高而降低.由于具有相对较低的热导率和较高的电导率,Ga2SnTe5在549 K时取得了最高ZT值0.16.
채용방전등리자소결기술(SPS)제비P형복상Ga2Te5기화합물,대기진행미관분석화열전성능측시.통과XRD분석관찰도주상Ga2Te5화소량적SnTe、단질Te.재정개측시온도(319～549 K)범위내,Ga2Te5기화합물적Seebeck계수、전도솔화열도솔도수온도적승고이강저.유우구유상대교저적열도솔화교고적전도솔,Ga2SnTe5재549 K시취득료최고ZT치0.16.
P-type Ga2Te5 based compounds with multiphase equilibrium were prepared by spark plasma sintering and their microstructures and thermoelectric properties were evaluated in the temperature range from 319 K to 549 K.Through XRD analysis,we observed the main phase Ga2Te5,a small amount of SnTe and single element Te were observed.Results indicate that the Seebeck coefficients increase and the electrical and thermal conductivities decrease with the increase of the temperature in the entire temperature range.The highest thermoelectric figure of merit ZTof 0.16 can be achieved for Ga2SnTe5 at 549 K due to relatively low thermal conductivity and high thermal conductivity.