CAJ | 학술논문

使用不同成分的Zn-Al钎料对铜铝异种金属进行火焰钎焊,研究其力学性能.利用光学显微镜、扫描电镜和能谱研究不同Zn-Al钎料对Cu/Al钎焊接头钎焊性、力学性能及显微组织的影响.结果表明:随着Al含量的增加,Zn-Al钎料在Cu和Al上的铺展面积逐渐增大.当钎料中Al含量为15％时,Cu/Al接头的抗剪强度达到最大值88 MPa;随着组织的变化,钎缝硬度值呈现HV122到HV515不等的分布.另外,钎缝组织的成分主要为富Zn相和富Al相,但是当钎料中Al含量为2％和15％以上时,靠近Cu侧的界面处会分别形成CuZn3和Al2Cu两种完全不同的金属间化合物.研究Zn-Al钎料中铝含量对Cu/Al接头界面化合物类型的影响.
사용불동성분적Zn-Al천료대동려이충금속진행화염천한,연구기역학성능.이용광학현미경、소묘전경화능보연구불동Zn-Al천료대Cu/Al천한접두천한성、역학성능급현미조직적영향.결과표명:수착Al함량적증가,Zn-Al천료재Cu화Al상적포전면적축점증대.당천료중Al함량위15％시,Cu/Al접두적항전강도체도최대치88 MPa;수착조직적변화,천봉경도치정현HV122도HV515불등적분포.령외,천봉조직적성분주요위부Zn상화부Al상,단시당천료중Al함량위2％화15％이상시,고근Cu측적계면처회분별형성CuZn3화Al2Cu량충완전불동적금속간화합물.연구Zn-Al천료중려함량대Cu/Al접두계면화합물류형적영향.
The mechanical properties and microstructural distribution of the Cu/Al brazing joints formed by torch-brazing with different Zn-Al filler metals were investigated.The microstructure of the Zn-Al alloys was studied by optical microscopy and scanning electron microscopy,and the phase constitution of the Cu/Al joints was analyzed by energy dispersion spectrometry.The results show that the spreading area of the Zn-Al filler metals on the Cu and Al substrates increases as the Al content increases.The mechanical results indicate that the shear strength reaches a peak value of 88 MPa when Al and Cu are brazed with Zn-15Al filler metal.Microhardness levels from HV122 to HV515 were produced in the three brazing seam regions corresponding to various microstructure features.The Zn- and Al-rich phases exist in the middle brazing seam regions.However,two interface layers,CuZn3 and Al2Cu are formed on the Cu side when the Al content in the filler metals is 2％ and more than 15％,respectively.The relationship between intermetallic compounds on Cu side and Zn-xAl filler metals was investigated.