DYEING AND FINISHING
2009年
15期
19-22
,共4页
张文化%王宗乾%郑荣兴%钟清
張文化%王宗乾%鄭榮興%鐘清
장문화%왕종건%정영흥%종청
前处理%酶%碱处理%再生纤维素纤维%Tencel
前處理%酶%堿處理%再生纖維素纖維%Tencel
전처리%매%감처리%재생섬유소섬유%Tencel
pretreatment%enzyme%alkali treatment%regenerated cellulosic fiber%Tencel
通过正交试验探讨碱氧一浴、原纤化和酶处理工艺对Tencel织物前处理质量的影响,分析不同质量浓度氢氧化钠处理对Tencd织物染色性能的影响.确定Tencel织物碱氧一浴法处理的优化工艺为:烧碱20g/L,精练剂科宁88 3 g/L,双氧水(27.5%)20 s/L,硅酸钠5g/L,稳定剂P5 g/L,渗透荆FR-M 1 g/L,络合剂28-A 2g/L,浴比1:20,90℃×30 min;原纤化优化工艺为:纯碱4 g/L,渗透剂FR-M 1 g/L,浴比1:20,90℃×30 min;酶处理优化工艺为:L40酶3 g/L,pH值7,渗透剂FR-M 1 g/L,浴比1:20,50℃×30 min.经该优化工艺处理,织物白度和毛效显著提高.此外,织物经苛化后,染色表观深度(K/S值)显著提高,合适的氢氧化钠浓度为100 g/L.
通過正交試驗探討堿氧一浴、原纖化和酶處理工藝對Tencel織物前處理質量的影響,分析不同質量濃度氫氧化鈉處理對Tencd織物染色性能的影響.確定Tencel織物堿氧一浴法處理的優化工藝為:燒堿20g/L,精練劑科寧88 3 g/L,雙氧水(27.5%)20 s/L,硅痠鈉5g/L,穩定劑P5 g/L,滲透荊FR-M 1 g/L,絡閤劑28-A 2g/L,浴比1:20,90℃×30 min;原纖化優化工藝為:純堿4 g/L,滲透劑FR-M 1 g/L,浴比1:20,90℃×30 min;酶處理優化工藝為:L40酶3 g/L,pH值7,滲透劑FR-M 1 g/L,浴比1:20,50℃×30 min.經該優化工藝處理,織物白度和毛效顯著提高.此外,織物經苛化後,染色錶觀深度(K/S值)顯著提高,閤適的氫氧化鈉濃度為100 g/L.
통과정교시험탐토감양일욕、원섬화화매처리공예대Tencel직물전처리질량적영향,분석불동질량농도경양화납처리대Tencd직물염색성능적영향.학정Tencel직물감양일욕법처리적우화공예위:소감20g/L,정련제과저88 3 g/L,쌍양수(27.5%)20 s/L,규산납5g/L,은정제P5 g/L,삼투형FR-M 1 g/L,락합제28-A 2g/L,욕비1:20,90℃×30 min;원섬화우화공예위:순감4 g/L,삼투제FR-M 1 g/L,욕비1:20,90℃×30 min;매처리우화공예위:L40매3 g/L,pH치7,삼투제FR-M 1 g/L,욕비1:20,50℃×30 min.경해우화공예처리,직물백도화모효현저제고.차외,직물경가화후,염색표관심도(K/S치)현저제고,합괄적경양화납농도위100 g/L.
Effects of one bath process of alkali and hydrogen peroxide, fibrillation process and enzyme treatment on pretreat-ment qualities of Tencel fabric were discussed, caustic soda treatment under different concentrsations was carried out to im-prove dyeability of Tencel fabric. Via orthogonal tests, optimal conditions were defined as follows: one bath process of alkali and hydrogen peroxide was: NaOH 20 g/L, Cognis 88 3 g/L, H2O2 20 g/L, Na2SiO3 5 g/L, stabihzer P 5 g/L, penetrating agent FR-M 1g/L, chelating agent 28-A 2 g/L, bath ratio 1:20, 90℃× 30 rain; fibrillation process: Na2CO3 4 g/L, penetrating agent FR-M 1 g/L,bath ratio 1 : 20, 90℃×30 min; enzyme treatment: enzyme L40 3 g/L, pH value 7, penetrating agent FR-M 1 g/L, bath ratio 1:20, 50 ℃×30 min. Tence[fabric after treatment featured good whiteness and absorbency, and little change in weight and strength. It was found that 100 g/L caustic soda treatment could greatly improve K/S values of the dyeings.