采用高温熔融的方法,在空气中制备了一系列添加不同网络修饰体氧化物的Eu2 O3和Dy2 O3共掺杂铝硼硅酸盐玻璃,并测试了其在紫外光激发下的发光性能.从发射谱中可以看到归属于Eu2+、Eu3+和Dy3+离子能级跃迁的蓝、绿、黄、红等多色发射带共存.这些发射带之间的相对强度会随着网络修饰体氧化物的改变而变化,从而导致发光色度的变化.加入适当的网络修饰体氧化物可得到合适的白光发射.此外,在空气中制备过程中发生了Eu3+→Eu3+的还原反应.用Li2O取代ZnO时,该还原反应程度降低,而用CaO取代BaO时该还原反应程度增强,其机制与玻璃组分的光碱度有关.
採用高溫鎔融的方法,在空氣中製備瞭一繫列添加不同網絡脩飾體氧化物的Eu2 O3和Dy2 O3共摻雜鋁硼硅痠鹽玻璃,併測試瞭其在紫外光激髮下的髮光性能.從髮射譜中可以看到歸屬于Eu2+、Eu3+和Dy3+離子能級躍遷的藍、綠、黃、紅等多色髮射帶共存.這些髮射帶之間的相對彊度會隨著網絡脩飾體氧化物的改變而變化,從而導緻髮光色度的變化.加入適噹的網絡脩飾體氧化物可得到閤適的白光髮射.此外,在空氣中製備過程中髮生瞭Eu3+→Eu3+的還原反應.用Li2O取代ZnO時,該還原反應程度降低,而用CaO取代BaO時該還原反應程度增彊,其機製與玻璃組分的光堿度有關.
채용고온용융적방법,재공기중제비료일계렬첨가불동망락수식체양화물적Eu2 O3화Dy2 O3공참잡려붕규산염파리,병측시료기재자외광격발하적발광성능.종발사보중가이간도귀속우Eu2+、Eu3+화Dy3+리자능급약천적람、록、황、홍등다색발사대공존.저사발사대지간적상대강도회수착망락수식체양화물적개변이변화,종이도치발광색도적변화.가입괄당적망락수식체양화물가득도합괄적백광발사.차외,재공기중제비과정중발생료Eu3+→Eu3+적환원반응.용Li2O취대ZnO시,해환원반응정도강저,이용CaO취대BaO시해환원반응정도증강,기궤제여파리조분적광감도유관.
Present work prepared a series of Eu2O3 and Dy2O3 co-doped aluminoborosilicate glasses with different network modifier addition by melting and annealing method.The emission spectra of these samples had been measured under UV light excitation.A combination of blue,green,yellow and red emission bands ascribed to transitions for Eu2+,Eu3+and Dy3+ions was shown for these glasses.It presented that the relative emission in-tensity could be adj usted with different network modifier oxides,and resulted in the change of luminescence col-or.White light emission could be obtained by appropriate network modifier oxides addition.Interestingly,it should be noted that the coexistence of Eu3+and Eu2+ions in the aluminoborosilicate glasses was observed ac-Cording to emission spectra.The Eu3+→Eu2+reduction degree decreased by substituting Li2O for ZnO,while it increased by substituting CaO for BaO.The change was discussed with the different optical basicity of the com-ponents.