CAJ | 학술논문

以丙烯酰胺(AM)为单体,N,N'-亚甲基双丙烯酰胺为交联剂,亚硫酸钠-过硫酸铵为引发剂,采用水溶液聚合法制备聚丙烯酰胺(PAM)吸湿材料.系统研究了单体浓度、交联剂用量和水解度等聚合条件对其吸湿性能的影响.吸湿实验表明,PAM的吸湿性能优于传统的无机吸湿材料硅胶和分子筛.采用聚乙二醇(PEG)、碳酸钙(CaCO_3)两种致孔剂合成多孔PAM,并与PAM的吸湿性能进行对比.实验结果知PAM/PEG的吸湿速率比PAM提高50%以上,吸湿容量也显著提高;而PAM/CaCO_3的吸湿效果并不理想.热失重分析TGA得出PAM/PEG比PAM的热稳定性稍稍降低,而PAM/CaCO_3的热稳定性则稍稍提高.
이병희선알(AM)위단체,N,N'-아갑기쌍병희선알위교련제,아류산납-과류산안위인발제,채용수용액취합법제비취병희선알(PAM)흡습재료.계통연구료단체농도、교련제용량화수해도등취합조건대기흡습성능적영향.흡습실험표명,PAM적흡습성능우우전통적무궤흡습재료규효화분자사.채용취을이순(PEG)、탄산개(CaCO_3)량충치공제합성다공PAM,병여PAM적흡습성능진행대비.실험결과지PAM/PEG적흡습속솔비PAM제고50%이상,흡습용량야현저제고;이PAM/CaCO_3적흡습효과병불이상.열실중분석TGA득출PAM/PEG비PAM적열은정성초초강저,이PAM/CaCO_3적열은정성칙초초제고.
In this paper,polyacrylamide (PAM) was synthesized with acrylamide as monomer,N,N'-methylene bisacrylamide as crosslinking agent ,sodium sulfite and ammonium persulfate as initiator by means of aqueous solution polymerization.The factors such as monomer concentration,hydrolysis degree,crossing-linking agent concentration and so on influencing on moisture absorbency were systematically investigated.Under the condition of T=20℃,RH=90%,the moisture absorption property of PAM was obviously better than the traditional materials,such as silica gel and molecular sieve.PAM/PEG and PAM/CaCO_3 porous materials were synthesized by using polyethylene glycol and calcium carbonate as pore-foaming agent respectively.Experimental results indicated that the moisture absorption rate of PAM/PEG was increased by more than 50% and its moisture absorption capacity was markedly improved than PAM too.Nevertheless,the moisture absorption ability of PAM/ CaCO_3 was not satisfactory.TGA analysis verified that the thermal stability of PAM/PEG was decreased but PAM/CaCO_3's got improved.