免缝线硅胶角膜环%理化性能%生物相容性
免縫線硅膠角膜環%理化性能%生物相容性
면봉선규효각막배%이화성능%생물상용성
sutureless silicone cornea ring%physicochemical properties%biocompatibility
背景玻璃体切割术中,角膜接触镜已得到广泛使用,配合接触镜使用的角膜环的改进也倍受关注.本课题组研制了一种新型免缝线的角膜环,其理化特性及生物相容性研究能为临床应用提供必要的理论依据.目的检测新型免缝线硅胶角膜环的理化性能特征和生物相容性.方法对新型免缝线硅胶角膜环进行邵氏硬度测试、拉伸应力应变测试、撕裂强度测试、透光率和雾度测试.收集人角膜上皮细胞进行细胞毒性分析以评价新型免缝线硅胶角膜环的生物相容性.6只成年白兔结膜囊内放置硅胶环产品,于6、24、48、72 h后记录白兔角膜荧光素着色面积以对硅胶环产品的刺激反应进行评价.6只成年SD大鼠备皮后皮肤表面放置硅胶环,并于6、24、48、72 h后测量SD大鼠局部皮肤红肿的面积以评价其过敏反应.结果新型免缝线硅胶角膜环的邵氏硬度为63.4度,拉伸强度大于5.86 MPa,伸长率大于100%,撕裂强度为34 kN/m.新型免缝线硅胶角膜环3爪的透光率均大于93%,而雾度均小于0.1%.免缝线硅胶角膜环对角膜细胞的细胞毒性测试值为3.11×10-6%.结膜囊内放置免缝线硅胶角膜环6、24、48、72 h,所有的兔眼均未见角膜荧光素着色.实验前及免缝线硅胶角膜环置于SD大鼠皮肤面后6、24、48、72 h,所有的SD大鼠皮肤均未见红肿.结论采用的硅橡胶理化特性能满足角膜环的制作要求,生物学评价符合ISO 10993-1评估医疗器材生物相容性的国际标准和生物体的要求,是制备角膜环较为理想的材料.
揹景玻璃體切割術中,角膜接觸鏡已得到廣汎使用,配閤接觸鏡使用的角膜環的改進也倍受關註.本課題組研製瞭一種新型免縫線的角膜環,其理化特性及生物相容性研究能為臨床應用提供必要的理論依據.目的檢測新型免縫線硅膠角膜環的理化性能特徵和生物相容性.方法對新型免縫線硅膠角膜環進行邵氏硬度測試、拉伸應力應變測試、撕裂彊度測試、透光率和霧度測試.收集人角膜上皮細胞進行細胞毒性分析以評價新型免縫線硅膠角膜環的生物相容性.6隻成年白兔結膜囊內放置硅膠環產品,于6、24、48、72 h後記錄白兔角膜熒光素著色麵積以對硅膠環產品的刺激反應進行評價.6隻成年SD大鼠備皮後皮膚錶麵放置硅膠環,併于6、24、48、72 h後測量SD大鼠跼部皮膚紅腫的麵積以評價其過敏反應.結果新型免縫線硅膠角膜環的邵氏硬度為63.4度,拉伸彊度大于5.86 MPa,伸長率大于100%,撕裂彊度為34 kN/m.新型免縫線硅膠角膜環3爪的透光率均大于93%,而霧度均小于0.1%.免縫線硅膠角膜環對角膜細胞的細胞毒性測試值為3.11×10-6%.結膜囊內放置免縫線硅膠角膜環6、24、48、72 h,所有的兔眼均未見角膜熒光素著色.實驗前及免縫線硅膠角膜環置于SD大鼠皮膚麵後6、24、48、72 h,所有的SD大鼠皮膚均未見紅腫.結論採用的硅橡膠理化特性能滿足角膜環的製作要求,生物學評價符閤ISO 10993-1評估醫療器材生物相容性的國際標準和生物體的要求,是製備角膜環較為理想的材料.
배경파리체절할술중,각막접촉경이득도엄범사용,배합접촉경사용적각막배적개진야배수관주.본과제조연제료일충신형면봉선적각막배,기이화특성급생물상용성연구능위림상응용제공필요적이론의거.목적검측신형면봉선규효각막배적이화성능특정화생물상용성.방법대신형면봉선규효각막배진행소씨경도측시、랍신응력응변측시、시렬강도측시、투광솔화무도측시.수집인각막상피세포진행세포독성분석이평개신형면봉선규효각막배적생물상용성.6지성년백토결막낭내방치규효배산품,우6、24、48、72 h후기록백토각막형광소착색면적이대규효배산품적자격반응진행평개.6지성년SD대서비피후피부표면방치규효배,병우6、24、48、72 h후측량SD대서국부피부홍종적면적이평개기과민반응.결과신형면봉선규효각막배적소씨경도위63.4도,랍신강도대우5.86 MPa,신장솔대우100%,시렬강도위34 kN/m.신형면봉선규효각막배3조적투광솔균대우93%,이무도균소우0.1%.면봉선규효각막배대각막세포적세포독성측시치위3.11×10-6%.결막낭내방치면봉선규효각막배6、24、48、72 h,소유적토안균미견각막형광소착색.실험전급면봉선규효각막배치우SD대서피부면후6、24、48、72 h,소유적SD대서피부균미견홍종.결론채용적규상효이화특성능만족각막배적제작요구,생물학평개부합ISO 10993-1평고의료기재생물상용성적국제표준화생물체적요구,시제비각막배교위이상적재료.
Background Corneal contact lens have been widely used in vitrectomy.The corneal ring accompanying with the contact lens therefore is also much concerned.We designed a sutureless silicone corneal ring to renew a suturing?ring,but its detection of physicochemical properties and hiocompatihility is necessary for clinical application. Objective This study was to investigate the physicochemical properties and biocompatibility of the newly designed sutureless silicone corneal ring. Methods The Shore hardness,tensile stress-strain tests,tear strength,transmittance and the haze of the novel silicone ring were tested.The bioeompatibility of sutureless silicone corneal ring to corneal epithelial cells was evaluated by determining cytotoxieity.The ring was implanted into the counjunctival soc of 6 Japanese white rabbits for 4 hours to determine its stimulation response by measuring the area of corneal fluorescence staining,and then the ring was placed on the skin surface of 6 SD rats for 4 hours to assess the presence of allergic reaction by calculating the swelling area of skin. Results The new sutureless silicone corneal ring showed good physiological features with a Shore hardness of 63.4 degree,tensile strength more than 5.86 MPa,elongation>100%and tear strength 34 kN/m.The transmittance of 3 legs in the ring was more than 93%;however,the haze was less than 0.1%.Cytotoxicity of the ring was 3.1 1×10-6%.No obvious corneal fluorescence staining was seen at any time point in all the rabbit eyes in the stimulating test.Furthermore,there was not any skin swelling in various time points in all the SD rats in the allergy test. Conclusion The physicochemical properties of the silastic used in our newly designed sutureless silicone cornea ring can meet the demands of the ring.The biological evaluation complies with the ISO i0993-1 international standards and meets the demands of the organism.Thus,it is all ideal material to use in constructing the corneal ring.