CAJ | 학술논문

为研究钢中添加稀土带来的夹杂物问题,采用金相夹杂物评级、电解夹杂分析以及电子探针和扫描电镜观察分析,对经稀土处理的微合金化碳锰钢夹杂物进行了研究.结果表明,采用铝脱氧和RH真空充分脱气的微合金化碳锰钢,经连铸结晶器喂稀土处理后,钢中的A,B,C,D类夹杂物分别不大于1.0级、1.5级、0.5级、1.5级,氧化物夹杂总量约为0.0030%.试验钢中主要形成球状稀土硫化物,同时还形成有链状"稀土硫化物包围氧化铝"的复合夹杂物,而稀土氧化物难以生成.
위연구강중첨가희토대래적협잡물문제,채용금상협잡물평급、전해협잡분석이급전자탐침화소묘전경관찰분석,대경희토처리적미합금화탄맹강협잡물진행료연구.결과표명,채용려탈양화RH진공충분탈기적미합금화탄맹강,경련주결정기위희토처리후,강중적A,B,C,D류협잡물분별불대우1.0급、1.5급、0.5급、1.5급,양화물협잡총량약위0.0030%.시험강중주요형성구상희토류화물,동시환형성유련상"희토류화물포위양화려"적복합협잡물,이희토양화물난이생성.
The inclusions in microalloying C-Mn steels with rare earths treating were investigated by means of optical microscopy, electrolytic inclusion analysis, EPMA and SEM. The results showed that the A, B, C and D type inclusions in the trial steels, which were treated by aluminum deoxidizing and RH vacuum de-gassing and then were fed by core- spun yarn of rare earths in continuous casting crystallizer, were not more than 1.0,1.5,0.5,1.5 grade respectively, and the total amount of oxide inclusions was about 0.0030%. The inclusions in the trial steel were mainly spherical rare-earth sulfides and chain compound inclusions of alumina surrounded by rare-earth sulfide, and at the same time, the rare earth oxides were difficult to gen-erate.