轮胎工业
輪胎工業
륜태공업
TIRE INDUSTRY
2009年
6期
360-363
,共4页
林浩%赵冬梅%程安仁%万淑霞
林浩%趙鼕梅%程安仁%萬淑霞
림호%조동매%정안인%만숙하
载重斜交轮胎%低滞后炭黑%胎面胶%胎肩胶
載重斜交輪胎%低滯後炭黑%胎麵膠%胎肩膠
재중사교륜태%저체후탄흑%태면효%태견효
bias truck tire%low hysteresis carbon black%tread compound%shoulder compound
研究低滞后炭黑DZ-13在载重斜交轮胎胎面胶和胎肩胶中的应用.结果表明,与采用炭黑N234或N375补强的硫化胶相比,采用低滞后炭黑DZ-13补强的硫化胶弹性模量和回弹值较大,滚动阻力较低,但撕裂强度和抗湿滑性能较差;低滞后炭黑DZ-13更适合用于胎肩胶.
研究低滯後炭黑DZ-13在載重斜交輪胎胎麵膠和胎肩膠中的應用.結果錶明,與採用炭黑N234或N375補彊的硫化膠相比,採用低滯後炭黑DZ-13補彊的硫化膠彈性模量和迴彈值較大,滾動阻力較低,但撕裂彊度和抗濕滑性能較差;低滯後炭黑DZ-13更適閤用于胎肩膠.
연구저체후탄흑DZ-13재재중사교륜태태면효화태견효중적응용.결과표명,여채용탄흑N234혹N375보강적류화효상비,채용저체후탄흑DZ-13보강적류화효탄성모량화회탄치교대,곤동조력교저,단시렬강도화항습활성능교차;저체후탄흑DZ-13경괄합용우태견효.
The application of low hysteresis carbon black DZ-13 in tread compound and shoulder compound of bias truck tire was investigated.The results showed that,compared to the vulcanizate reinforced by carbon black N234 or N375,the vulcanizate reinforced by low hysteresis carbon black DZ-13 possessed higher elastic modulus and rebound value,lower rolling resistance,but it also showed poorer tear strength and wet skid resistance;the low hysteresis carbon black DZ-13 was more suitable for the shoulder compound.