采用溶胶-凝胶法制备了Nd0.6_xBaxSr0.4Co0.2Fe0.803-δ(x =0,0.05,0.10,0.15,0.20,NBSCF)粉体与电解质粉体Ce0.8Sm0201.9(SDC),利用X射线衍射仪、热膨胀仪分别对材料的晶体结构和烧结陶瓷体的热膨胀系数(TEC)进行表征.以不同组分的NBSCF-30％ SDC为复合阴极,以SDC为电解质,用交流阻抗法测试了550 ～ 750℃范围内对称电极的极化电阻.结果表明,合成的NBSCF粉体均形成了单相正交钙钛矿结构.随着Ba含量的增加,材料的热膨胀系数增大,复合阴极的极化电阻减小.当x =0.20时,NBSCF-30％ SDC复合阴极的极化电阻最小,750℃时为0.032Ω·cm2.
채용용효-응효법제비료Nd0.6_xBaxSr0.4Co0.2Fe0.803-δ(x =0,0.05,0.10,0.15,0.20,NBSCF)분체여전해질분체Ce0.8Sm0201.9(SDC),이용X사선연사의、열팽창의분별대재료적정체결구화소결도자체적열팽창계수(TEC)진행표정.이불동조분적NBSCF-30％ SDC위복합음겁,이SDC위전해질,용교류조항법측시료550 ～ 750℃범위내대칭전겁적겁화전조.결과표명,합성적NBSCF분체균형성료단상정교개태광결구.수착Ba함량적증가,재료적열팽창계수증대,복합음겁적겁화전조감소.당x =0.20시,NBSCF-30％ SDC복합음겁적겁화전조최소,750℃시위0.032Ω·cm2.