材料开发与应用
材料開髮與應用
재료개발여응용
DEVELOPMENT AND APPLICATION OF MATERIALS
2009年
1期
4-7
,共4页
气阀钢%Al-Cr二元渗层%Al-Cr-Ce三元渗层%显微组织%显微硬度%渗层厚度
氣閥鋼%Al-Cr二元滲層%Al-Cr-Ce三元滲層%顯微組織%顯微硬度%滲層厚度
기벌강%Al-Cr이원삼층%Al-Cr-Ce삼원삼층%현미조직%현미경도%삼층후도
用固体粉末法,在4Cr10Si2Mo马氏体气阀钢表面制备了AJ-Cr二元渗层及Al-Cr-Ce三元渗层,研究了渗层的显微组织和成分分布,测定了渗层由表及里的显微硬度.Al-Cr渗层厚度约为35μm,硬度为580Hv;Al-Cr-Ce渗层厚度约为420μm,硬度为500Hv.
用固體粉末法,在4Cr10Si2Mo馬氏體氣閥鋼錶麵製備瞭AJ-Cr二元滲層及Al-Cr-Ce三元滲層,研究瞭滲層的顯微組織和成分分佈,測定瞭滲層由錶及裏的顯微硬度.Al-Cr滲層厚度約為35μm,硬度為580Hv;Al-Cr-Ce滲層厚度約為420μm,硬度為500Hv.
용고체분말법,재4Cr10Si2Mo마씨체기벌강표면제비료AJ-Cr이원삼층급Al-Cr-Ce삼원삼층,연구료삼층적현미조직화성분분포,측정료삼층유표급리적현미경도.Al-Cr삼층후도약위35μm,경도위580Hv;Al-Cr-Ce삼층후도약위420μm,경도위500Hv.