共沉淀法合成了层状Li1+xNi0.8Co0.2O2(x=0和 0.05),采用XRD和电化学方法对其进行了研究.与LiNi0.8Co0.2O2相比,Li1.05Ni0.8Co0.2O2有较高的放电容量和较差的循环性能.与LiNi0.8Co0.2O2放电容量微分曲线相似,Li1.05Ni0.8Co0.2O2在4.15 V存在负峰,随着循环次数的增加,4.15 V负峰峰位明显向左移.与LiNi0.8Co0.2O2放电容量微分曲线不同,层状结构Li1.05Ni0.8Co0.2O2的4.15 V负峰峰高随循环次数的增加而增高,循环过程促进了Li1.05Ni0.8Co0.2O2结构转变.
공침정법합성료층상Li1+xNi0.8Co0.2O2(x=0화 0.05),채용XRD화전화학방법대기진행료연구.여LiNi0.8Co0.2O2상비,Li1.05Ni0.8Co0.2O2유교고적방전용량화교차적순배성능.여LiNi0.8Co0.2O2방전용량미분곡선상사,Li1.05Ni0.8Co0.2O2재4.15 V존재부봉,수착순배차수적증가,4.15 V부봉봉위명현향좌이.여LiNi0.8Co0.2O2방전용량미분곡선불동,층상결구Li1.05Ni0.8Co0.2O2적4.15 V부봉봉고수순배차수적증가이증고,순배과정촉진료Li1.05Ni0.8Co0.2O2결구전변.