以Pb(NO3)2和KSCN为原料,水为溶剂,采用水热法制备出了三维的八足状PbS树枝晶.XRD测试表明粉体为面心立方结构,结晶性好;SEM照片显示粉体为八足状的三维超结构,每足的平均长度5 μm,由边长600～800 nm的片状纳米块自组装而成.结合PbS晶体的结构模型和样品SEM照片的跟踪观察,分析了八足状PbS树枝晶的生长演变过程,为超结构微晶的生长机理研究提供有益参考.
이Pb(NO3)2화KSCN위원료,수위용제,채용수열법제비출료삼유적팔족상PbS수지정.XRD측시표명분체위면심립방결구,결정성호;SEM조편현시분체위팔족상적삼유초결구,매족적평균장도5 μm,유변장600～800 nm적편상납미괴자조장이성.결합PbS정체적결구모형화양품SEM조편적근종관찰,분석료팔족상PbS수지정적생장연변과정,위초결구미정적생장궤리연구제공유익삼고.
Three dimensional (3D) octa-pod-like PbS dendrites were controllably prepared by hydrothermal method using Pb(NO3)2 and KSCN as raw materials. X-ray diffraction (XRD) pattern indicates that the as-prepared products are of face-centered cubic phase structure and crystallize very well. Scanning electron microscope (SEM) images show that the as-obtained samples mainly take on 3D superstructures with eight pods. Each pod has average diameter of about 5 μm, which self-assembled by flake-like cube with edge lengths of 600-800 nm. Based on the schematic pattern of PbS crystals and SEM observation connected with the reaction time, The shape evolution process of the octa-pod-like PbS dendrites was investigated, which may provide beneficial reference for studying the growth mechanism of some microcrystals with superstructure.