The effect of heat treatment mode on the microstructure of Fe-Cr-B east iron alloys was investigated in this paper by comparing the difference of precipitation pattems of secondary particles after thermal cycling treatment (TCT) with those after normal heat treatment (NHT). No obvious differences were found in precipitation pattems of secondary particles between TCT and NHT when experimental temperature was below ArI. However, when temperature was over Ar1, there were significant differences, with secondary particles prominently segregated at the grain boundaries under TCT, while the particles evenly distributed in the matrix under NHT. The mason for the microstructure differences could be associated with the development of non-equilibrium segregation of boron during TCT.