以3釜串联连续本体聚合工艺合成了(丙烯腈/丁二烯/苯乙烯)共聚物(ABS),并研究了其力学性能.结果表明,在一定橡胶含量条件下,采用双嵌段丁苯橡胶替代聚丁二烯橡胶可使ABS树脂的综合力学性能得以提高;双嵌段丁苯橡胶质量分数每增加0.1%,可使ABS树脂的冲击强度提高约0.98～1.67 kJ/m~2,但其耐热性有所下降,拉伸强度和弯曲强度存在峰值.为获得均衡的性能,(苯乙烯/丙烯腈)共聚物(SAN)树脂相重均相对分子质量应控制在2.0×10~5～2.5×10~5,高于2.5×10~5之后,ABS树脂性能提升不明显.与乳液法ABS树脂相比,连续本体法ABS树脂具有极低的残余单体含量,有明显的环保优势.
이3부천련련속본체취합공예합성료(병희정/정이희/분을희)공취물(ABS),병연구료기역학성능.결과표명,재일정상효함량조건하,채용쌍감단정분상효체대취정이희상효가사ABS수지적종합역학성능득이제고;쌍감단정분상효질량분수매증가0.1%,가사ABS수지적충격강도제고약0.98～1.67 kJ/m~2,단기내열성유소하강,랍신강도화만곡강도존재봉치.위획득균형적성능,(분을희/병희정)공취물(SAN)수지상중균상대분자질량응공제재2.0×10~5～2.5×10~5,고우2.5×10~5지후,ABS수지성능제승불명현.여유액법ABS수지상비,련속본체법ABS수지구유겁저적잔여단체함량,유명현적배보우세.
The synthesis and property analysis of continuous mass ABS are discussed. The results indicate that the bi-block styrene-butadiene rubber, instead of poly-butadiene rubber, can improve the general mechanical properties of ABS. Every 0.1% increment of bi-block styrene-butadiene rubber content will increase the impact property by 0.98-1.67kJ/m~2. In order to get general properties with ideal balance, the molecular weight of the matrix resin should be confined to 2.0×10~5-2.5×10~5. The ABS resin made by mass process has extremely low content of residual monomers.