研究了金属钛与聚碳硅烷陶瓷先驱体作为原料原位制备Si-C-Ti陶瓷.分析了二者比例、热解温度等对合成产物组成的影响.利用扫描电镜(SEM)结合能谱分析(EDX)对合成的产物的微观结构和组成进行了表征.首次发现金属钛与聚碳硅烷陶瓷先驱体反应形成Ti_3SiC_2相,利用DSC、XRD对金属钛与聚碳硅烷的反应温度及在不同温度下反应产物的组成进行表征,分析了Ti_3SiC_2相的形成机理.研究发现,可以通过控制先驱体与金属的比例及工艺条件等合成高纯的Ti_3SiC_2.
연구료금속태여취탄규완도자선구체작위원료원위제비Si-C-Ti도자.분석료이자비례、열해온도등대합성산물조성적영향.이용소묘전경(SEM)결합능보분석(EDX)대합성적산물적미관결구화조성진행료표정.수차발현금속태여취탄규완도자선구체반응형성Ti_3SiC_2상,이용DSC、XRD대금속태여취탄규완적반응온도급재불동온도하반응산물적조성진행표정,분석료Ti_3SiC_2상적형성궤리.연구발현,가이통과공제선구체여금속적비례급공예조건등합성고순적Ti_3SiC_2.
Study on the preparation of Si-C-Ti ceramic by in-situ reaction between polycarbosilane(PCS) and metal Ti had been proceeded in this work. The effects of their ratios and reactive condition on the composition of pyrolytic products were studied. The Ti_3SiC_2 phase formed by reaction between metal Ti and PCS was firstly observed. The reaction temperature between (PCS) and metal Ti and compositions of products obtained at different temperature were examined by DSC and XRD. The formed mechanism for Ti_3SiC_2 was analyzed. The results indicated that the high-purity Ti_3SiC_2 can be obtained by controlling the ratios between PCS and metal Ti and reaction conditions. The morphology and composition were characterized by SEM with EDX.