目的:观察3 种粘接瓷对钛瓷结合强度的影响,分析粘接瓷作用机制.方法:将纯钛试件随机分为3 组分别采用纯钛专用瓷Super Ti22,Duceratin,Titankeramik进行烧结,每种瓷粉又分为涂布粘接瓷组和未涂布粘接瓷组,共6 组.根据ISO9693标准,运用三点弯曲方法测试各组钛瓷结合强度.对钛瓷结合界面进行扫描电镜观察和能谱分析.结果:Super Ti22涂布粘接瓷组结合强度为(35.84±2.17) MPa,Duceratin涂布粘接瓷组结合强度为(35.45±2.37) MPa,均显著大于各自未涂布组(P<0.05);Titankeramik涂布粘接瓷组结合强度为(31.73±1.66) MPa, 略大于其未涂布组(29.86±2.48) MPa,但差异无显著性(P>0.05).电镜观察Super Ti22和Duceratin涂布粘接瓷组钛瓷结合界面结合紧密,未见明显孔隙出现;其余各组均可见明显孔隙.结论:粘接瓷的应用有利于钛瓷结合强度的提高.
目的:觀察3 種粘接瓷對鈦瓷結閤彊度的影響,分析粘接瓷作用機製.方法:將純鈦試件隨機分為3 組分彆採用純鈦專用瓷Super Ti22,Duceratin,Titankeramik進行燒結,每種瓷粉又分為塗佈粘接瓷組和未塗佈粘接瓷組,共6 組.根據ISO9693標準,運用三點彎麯方法測試各組鈦瓷結閤彊度.對鈦瓷結閤界麵進行掃描電鏡觀察和能譜分析.結果:Super Ti22塗佈粘接瓷組結閤彊度為(35.84±2.17) MPa,Duceratin塗佈粘接瓷組結閤彊度為(35.45±2.37) MPa,均顯著大于各自未塗佈組(P<0.05);Titankeramik塗佈粘接瓷組結閤彊度為(31.73±1.66) MPa, 略大于其未塗佈組(29.86±2.48) MPa,但差異無顯著性(P>0.05).電鏡觀察Super Ti22和Duceratin塗佈粘接瓷組鈦瓷結閤界麵結閤緊密,未見明顯孔隙齣現;其餘各組均可見明顯孔隙.結論:粘接瓷的應用有利于鈦瓷結閤彊度的提高.
목적:관찰3 충점접자대태자결합강도적영향,분석점접자작용궤제.방법:장순태시건수궤분위3 조분별채용순태전용자Super Ti22,Duceratin,Titankeramik진행소결,매충자분우분위도포점접자조화미도포점접자조,공6 조.근거ISO9693표준,운용삼점만곡방법측시각조태자결합강도.대태자결합계면진행소묘전경관찰화능보분석.결과:Super Ti22도포점접자조결합강도위(35.84±2.17) MPa,Duceratin도포점접자조결합강도위(35.45±2.37) MPa,균현저대우각자미도포조(P<0.05);Titankeramik도포점접자조결합강도위(31.73±1.66) MPa, 략대우기미도포조(29.86±2.48) MPa,단차이무현저성(P>0.05).전경관찰Super Ti22화Duceratin도포점접자조태자결합계면결합긴밀,미견명현공극출현;기여각조균가견명현공극.결론:점접자적응용유리우태자결합강도적제고.
Objective:To evaluate the effects of three bond agents on bond strength of titanium- ceramic system. Methods: The pure titanium specimens were randomly divided into three groups. Three different manufacturers' porcelains(Super Ti22,Duceratin,Titankeramik) were used specially for titanium- ceramic bonding. The specimens in each group were further divided into two subgroups:bond agent group and no bond agent group. Bond strength of specimens was measured by the three- point bending test according to ISO9693. The titanium- ceramic interfaces were investigated by SEM/EDS. Results:The bond strength of Super Ti22(35.84±2.17) MPa and Duceratin(35.45±2.37) MPa with bond agent group was significantly higher than that of no bond agent group(P<0.05). Titankeramik with bond agent group showed a little higher bond strength than without bond agent, but no significant difference in statistics(P>0.05). The interfaces of Super Ti22 and Duceratin with bond agent groups were compact, while there were visible cracks and pores at the interface of other groups. Conclusion:The application of bond agent can improve bond strength of titanium- ceramic system.