The TiC/Ni composite coating was prepared by laser cladding in-situ synthesis on the surface of damper plate with Ni-Cr-Ti-C-LaF_3 powder.Micmstrueture and corrosion resistance were studied through SEM and M352 electrochemistry corrosion system.The result shows that both the coating without LaF_3 and the coating with 3%LaF_3 have the heterogeneous phase;the corrosion current of the two coating elevates,the corrosion potential and corrosion resistance reduces.The laser cladding with 2%LaF_3 has no heterogeneous phases,which reduces the corrosion current,elevates the corrosion potential and increases the width ofpassivation area.So the corrosion resistance improves.