The "fin-burning" phenomenon of aluminum air-conditioning condenser after brazed was introduced, a detailed analysis for morphology of brazed joint and the causes of this phenomenon were given. The causes were analyzed from two aspects: the raw materials and process parameters of brazing. The results of experiments and analysis indicate that the thicker solder layer, minor scratches on the surface of flat tube and unreasonable brazing process parameters can cause the disappearance of fin. It provides a theory basis for getting well brazed joints of condenser.