C/C复合材料%化学气相渗透(CVI)%高密度预制体%弯曲力学性能%断裂机制
C/C複閤材料%化學氣相滲透(CVI)%高密度預製體%彎麯力學性能%斷裂機製
C/C복합재료%화학기상삼투(CVI)%고밀도예제체%만곡역학성능%단렬궤제
C/C composites%chemical vapor infiltration (CVI)%high density preform%bending prop erties%fracture mechanism
以丙烯作为碳源,氮气作为载气,采用初始密度为0.94 g/cm3三维正交PAN基12 K炭纤维预制体,利用自制的快速CVI炉制备基体热解炭结构为带状结构的C/C复合材料.力学性能测试结果表明,材料的弯曲断裂特征与制备过程中受到的高温热处理次数有关.从载荷-位移曲线来看,当C/C复合材料经过两次热处理时,C/C复合材料呈明显假塑性断裂特征.当C/C复合材料经过三次热处理时,载荷-位移曲线趋于稳定平滑,抗弯强度降低.从C/C复合材料断面的SEM图可以观察到材料断裂可以分为层间断裂和层内断裂,而层内断裂又因热解炭填充密度变化呈明显的分区断裂.由于热解炭和纤维含量在C/C复合材料中分布的差异,材料在不同的区域表现出不同的断裂特征,从而使得材料具备良好的弯曲强度同时具有一定的韧性特征.
以丙烯作為碳源,氮氣作為載氣,採用初始密度為0.94 g/cm3三維正交PAN基12 K炭纖維預製體,利用自製的快速CVI爐製備基體熱解炭結構為帶狀結構的C/C複閤材料.力學性能測試結果錶明,材料的彎麯斷裂特徵與製備過程中受到的高溫熱處理次數有關.從載荷-位移麯線來看,噹C/C複閤材料經過兩次熱處理時,C/C複閤材料呈明顯假塑性斷裂特徵.噹C/C複閤材料經過三次熱處理時,載荷-位移麯線趨于穩定平滑,抗彎彊度降低.從C/C複閤材料斷麵的SEM圖可以觀察到材料斷裂可以分為層間斷裂和層內斷裂,而層內斷裂又因熱解炭填充密度變化呈明顯的分區斷裂.由于熱解炭和纖維含量在C/C複閤材料中分佈的差異,材料在不同的區域錶現齣不同的斷裂特徵,從而使得材料具備良好的彎麯彊度同時具有一定的韌性特徵.
이병희작위탄원,담기작위재기,채용초시밀도위0.94 g/cm3삼유정교PAN기12 K탄섬유예제체,이용자제적쾌속CVI로제비기체열해탄결구위대상결구적C/C복합재료.역학성능측시결과표명,재료적만곡단렬특정여제비과정중수도적고온열처리차수유관.종재하-위이곡선래간,당C/C복합재료경과량차열처리시,C/C복합재료정명현가소성단렬특정.당C/C복합재료경과삼차열처리시,재하-위이곡선추우은정평활,항만강도강저.종C/C복합재료단면적SEM도가이관찰도재료단렬가이분위층간단렬화층내단렬,이층내단렬우인열해탄전충밀도변화정명현적분구단렬.유우열해탄화섬유함량재C/C복합재료중분포적차이,재료재불동적구역표현출불동적단렬특정,종이사득재료구비량호적만곡강도동시구유일정적인성특정.
C/C composites with banded structure pyroearbon were fabricated by fast chemical vapor infiltration (CVI),with C3H6 as carbon source,N2 as carrier gas,and three-dimensional (3D) 12K PAN-based carbon fabric with high density of 0.94 g/cm3 as preform.Experimental results indicated that the fracture characteristics of C/C composites were closely related to the frequency of high-temperature treatment (HTT) at the break of CVI process.According to the load-displacement curves,C/C composites showed a pseudoplastic fracture after twice of HTT.After three times of HTT,load-displacement curves tended to be stable with a decreasing bending strength at 177.5 MPa.Delamination failure and intrastratal fiber fracture were observed at the cross-section of C/C composites by scanning electronic microscope.Because the content of pyrocarbon and fibers has a different distribution in layers,the C/C composites show different fracture characteristics at various regions,which leads to good toughness and bending strength.