铜包铝复合棒%有限元分析%平辊轧制%宽展
銅包鋁複閤棒%有限元分析%平輥軋製%寬展
동포려복합봉%유한원분석%평곤알제%관전
copper cladding aluminum composite rod%finite element analysis%flat rolling%spreading
对铜包铝复合棒材平辊冷轧时的金属流动进行数值模拟和实验研究.结果表明:由圆断面至扁断面的第一道次平辊轧制中侧边以变形宽展为主;在后续道次的平辊轧制过程中,滑动宽展的影响增大,侧边变形宽展的影响减小;当压下率为13.3%~26.7%时,摩擦因数对铜包铝棒材宽展率的影响较小,而当压下率大于33.3%时,摩擦因数对宽展的影响增大;铜包铝复合棒材的最大轧制压力在轧制入口端,断面上存在一条"X"状的等效应变带.实验结果与有限元分析结果具有良好的一致性.采用合适的轧制工艺,可获得铜包覆层分布均匀、铜铝复合界面无裂纹和分层、表面质量好的扁排.
對銅包鋁複閤棒材平輥冷軋時的金屬流動進行數值模擬和實驗研究.結果錶明:由圓斷麵至扁斷麵的第一道次平輥軋製中側邊以變形寬展為主;在後續道次的平輥軋製過程中,滑動寬展的影響增大,側邊變形寬展的影響減小;噹壓下率為13.3%~26.7%時,摩抆因數對銅包鋁棒材寬展率的影響較小,而噹壓下率大于33.3%時,摩抆因數對寬展的影響增大;銅包鋁複閤棒材的最大軋製壓力在軋製入口耑,斷麵上存在一條"X"狀的等效應變帶.實驗結果與有限元分析結果具有良好的一緻性.採用閤適的軋製工藝,可穫得銅包覆層分佈均勻、銅鋁複閤界麵無裂紋和分層、錶麵質量好的扁排.
대동포려복합봉재평곤랭알시적금속류동진행수치모의화실험연구.결과표명:유원단면지편단면적제일도차평곤알제중측변이변형관전위주;재후속도차적평곤알제과정중,활동관전적영향증대,측변변형관전적영향감소;당압하솔위13.3%~26.7%시,마찰인수대동포려봉재관전솔적영향교소,이당압하솔대우33.3%시,마찰인수대관전적영향증대;동포려복합봉재적최대알제압력재알제입구단,단면상존재일조"X"상적등효응변대.실험결과여유한원분석결과구유량호적일치성.채용합괄적알제공예,가획득동포복층분포균균、동려복합계면무렬문화분층、표면질량호적편배.
Combining finite element simulation with experiments, the metal flow behavior in cold flat rolling of copper cladding aluminum(CCA) composite rod was investigated. The results show that sidepiece deformation spreading is dominant in the first flat rolling pass. However, in the later passes, the influence of slip spreading enhances while the influence of sidepiece deformation spreading reduces. When the rolling reduction ratio is in the range of 13.3%-26.7%, the influence of friction factor on lateral spreading rate is small, but when the ratio is larger than 36.7%, the influence increases. The maximum pressure lies at the entry of rod rolling. There is an "X" like equivalent strain zone in the section. Reasonable agreement of the FEM analysis and the experimental results is obtained. CCA flat bar that has clean surface quality and uniform thickness of copper cladding layer, without crack and layer at the composite interface, can be prepared by property rolling process.