The CuZrAl bulk metallic glass with minor-addition of Fe was prepared by rapid quenching method.The structures were examined by X-ray diffraction (XRD).The effect of Fe on the glass-forming ability was studied by differential scanning calorimetry (DSC).The minor-addition of Fe obviously extends the supercooled liquid region △Tx.The plastic strain of the Cu44Zr48Al7Fe bulk metallic glass is about 1.5％.The microstructures were examined by transmission electron microscopy (TEM).It is found that when 1％-2％ Fe (mole fraction) were introduced into the CuZrAl alloy matrix nanoscale phase separation occurs in the as-prepared Cu44Zr48Al7Fe bulk metallic glass.