采用自制温和前处理助剂STP-A对聚苯硫醚(PPS)纤维织物进行退、煮、漂一步法前处理,优化工艺为:STP-A 4 g/L,H_2O_2(100%)3 g/L,渗透剂3 g/L,pH值8,浴比1:20,95℃×90 min;对PPS纤维织物进行分散染料载体染色,优化工艺为:载体3 g/L,染料2%(owf),高温匀染剂TF-203 1 g/L,pH值4.5～5,浴比1:30,120～130℃×90 min.生产实践表明,PPS纤维产品具有理想的染色深度和色牢度,染整加工不会影响其阻燃性.
채용자제온화전처리조제STP-A대취분류미(PPS)섬유직물진행퇴、자、표일보법전처리,우화공예위:STP-A 4 g/L,H_2O_2(100%)3 g/L,삼투제3 g/L,pH치8,욕비1:20,95℃×90 min;대PPS섬유직물진행분산염료재체염색,우화공예위:재체3 g/L,염료2%(owf),고온균염제TF-203 1 g/L,pH치4.5～5,욕비1:30,120～130℃×90 min.생산실천표명,PPS섬유산품구유이상적염색심도화색뇌도,염정가공불회영향기조연성.
One-step mild pretreatment of desizing,scouring and bleaching was carried out on PPS fiber fabric with a self-made agent STP-A.The optimum pretreatment process was STP-A4 g/L,H_2O_2 (100%)3 g/L,penetrating agent 3 g/L,pretreatment at 95℃ for 90 minutes with pH value 8 and bath ratio 1:20.Carrier dyeing with disperse dyes was chosen,and the optimum process was self-made carrier STZT-1 3 g/L,dyes 2%(owf),levelling agent TF- 203 1 g/L,dyeing at 120 ～ 130 ～C for 90 mi-nutes with pH value 4.5～5 and bath ratio 1:30.Practical application showed that PPS product had desirable color depth and fastness,and wet processing did no harm to flame retardancy of PPS fiber.