采用高温坩埚下降法生长La2 Ti2 O7晶体,获得的晶体尺寸约为18 mm× 12 mm× 10 mm,其表面出现了一系列(004)解理面.X射线双摇摆曲线表明该晶体具有良好的结晶质量.透过光谱显示退火后的La2 Ti2 O7晶体在可见光范围内是透明的,当波长在800 nm左右时,透过率将显著下降.La2 Ti2 O7晶体的吸收边出现在500 nm波长附近.光折射指数分析表明退火La2 Ti2 O7晶体具有高的折射率.折射率色散方程确定为n2(λ) =4.61643 +0.16198/(λ2-0.01547) -0.47201λ2,利用该公式可计算出300～1680 nm范围内任意波长下的折射指数n值.
채용고온감과하강법생장La2 Ti2 O7정체,획득적정체척촌약위18 mm× 12 mm× 10 mm,기표면출현료일계렬(004)해리면.X사선쌍요파곡선표명해정체구유량호적결정질량.투과광보현시퇴화후적La2 Ti2 O7정체재가견광범위내시투명적,당파장재800 nm좌우시,투과솔장현저하강.La2 Ti2 O7정체적흡수변출현재500 nm파장부근.광절사지수분석표명퇴화La2 Ti2 O7정체구유고적절사솔.절사솔색산방정학정위n2(λ) =4.61643 +0.16198/(λ2-0.01547) -0.47201λ2,이용해공식가계산출300～1680 nm범위내임의파장하적절사지수n치.
La2Ti2O7 crystal has been grown by a high-temperature vertical Bridgman method. The as-grown crystal is about 18 mm x 12 mm x 10 mm in dimensions with a series of (004) cleavage planes on the surface. X-ray rocking curve reveals that the crystal has excellent crystalline quality. Transmission spectra implies the nnealed La2Ti2O7 crystal is transparent in visible region and drops down quickly near 800 nm. The optical absorption edge is around 500 nm. Refractive index analysis emonstrates the annealed La2Ti2O7 crystal has high refractive property. The dispersion relation is determined to be n2 ( A ) = 4. 61643 +0. 16198/ (A2_0.01547) - 0. 4720IA2 which can be used to calculate the refractive indexn value at any wavelength in the range of 300-1680 nm.