利用无压浸渗法制备高体积分数的SiCp/Al复合材料.采用X射线衍射(XRD)和扫描电镜(SEM)对复合材料的相组成、微观组织及断口形貌进行分析,研究了基体合金成分对复合材料抗弯性能的影响.结果表明,以Al-10%Si-8%Mg合金为基体制备的复合材料组织均匀,致密度好,无明显气孔缺陷,界面反应产物为Mg_2Si、MgAl_2O_4和Fe,且抗弯强度高于以Al-10%Si合金为基体制备的复合材料;复合材料整体上表现出脆性断裂的特征.
이용무압침삼법제비고체적분수적SiCp/Al복합재료.채용X사선연사(XRD)화소묘전경(SEM)대복합재료적상조성、미관조직급단구형모진행분석,연구료기체합금성분대복합재료항만성능적영향.결과표명,이Al-10%Si-8%Mg합금위기체제비적복합재료조직균균,치밀도호,무명현기공결함,계면반응산물위Mg_2Si、MgAl_2O_4화Fe,차항만강도고우이Al-10%Si합금위기체제비적복합재료;복합재료정체상표현출취성단렬적특정.
High volume fraction SiCp/Al composites were fabricated by pressureless infiltration technique.The effect of aluminum matrix on the bending strength of the composites was studied.The microstructures and the fracture morphology of composites were observed by SEM and the components were analyzed by XRD.The results show that the microstructures in the SiCp/Al-10Si-8Mg composite were quite uniform and appeared to be free of pores and the interfacial reaction products were Mg_2Si,MgAl_2O_4 and Fe.The bending strength of SiCp/Al-10Si-8Mg composite was better than the SiCp/Al-10Si composite.Composites have the character of brittleness fracture.