采用真空电弧熔炼法制得式为Ni46Ti44Ta10(at%)的锭子,经过均匀化处理后,轧制成板材用作试样;采用DSC,XRD,SEM以及显微硬度测试等试验手段,对经时效处理的新型Ni-Ti-Ta形状记忆合金的性能进行了研究.结果表明:在300℃～550℃对Ni46Ti44Ta10合金进行时效处理后,有Ti11Ni14沉淀相析出,并且产生沉淀硬化效应;合金的相变温度和硬化程度随着时效处理的参数的不同而不同;经适当的时效处理,该合金不仅具有优越的形状记忆效应,而且可以达到最好的硬化效果.
채용진공전호용련법제득식위Ni46Ti44Ta10(at%)적정자,경과균균화처리후,알제성판재용작시양;채용DSC,XRD,SEM이급현미경도측시등시험수단,대경시효처리적신형Ni-Ti-Ta형상기억합금적성능진행료연구.결과표명:재300℃～550℃대Ni46Ti44Ta10합금진행시효처리후,유Ti11Ni14침정상석출,병차산생침정경화효응;합금적상변온도화경화정도수착시효처리적삼수적불동이불동;경괄당적시효처리,해합금불부구유우월적형상기억효응,이차가이체도최호적경화효과.
An attempt was made to improve the shape memory characteristics for new non-equiatomic Ni-Ti-Ta shape memory alloysadopting heat treatment. The ingot with composition of Ni46Ti44Ta10(at% ) was prepared by vacuum are melting, then homogenized,finally was rolled into the sheet used as the samples. The characteristics were studied by differential scanning calorimetry (DSC),microhardness testing, X-ray diffracometer and scanning electron microscopy (SEM). Results show that Ti11Ni14 precipitates can beproduced by an aging treatment in the temperature range from 300℃ to 550℃ for the alloy. Meanwhile, precipitation hardeningoccurred during the aging process. The phase transformation temperatures and hardness of experimental alloys vary with changing ofaging parameters. The enhanced shape memory effect was obtained in aged samples, with the best shape memory effect corre-sponding to the highest hardness value.