溶剂萃取%伯胺7101%五氧化二钒
溶劑萃取%伯胺7101%五氧化二釩
용제췌취%백알7101%오양화이범
solvent extraction%primary amine 7101%vanadium
研究了用伯胺7101从钒渣浸出液中萃取钒,考察了萃取剂组成、两相接触时间对钒萃取率的影响,以及反萃取剂组成、温度及两相接触时间对钒反萃取率的影响。试验结果表明:对于钒质量浓度为17 g/L的钒净化液,用10%7101+10%仲辛醇+80%煤油作萃取剂,在常温、相比V o/V a=1/1条件下萃取5 min ,钒萃取率在90%以上,萃取剂饱和容量为29.5 g/L ;对于负载17.0 g/L钒的有机相,用170 g/L的(N H4)2 CO3溶液作反萃取剂反萃取沉淀钒,控制相比V o/V a =1/1,温度为35~40℃,两相接触15 min ,钒的反萃取率达99%,所得五氧化二钒产品质量质量优于YB/T5304-2011冶金99级标准。
研究瞭用伯胺7101從釩渣浸齣液中萃取釩,攷察瞭萃取劑組成、兩相接觸時間對釩萃取率的影響,以及反萃取劑組成、溫度及兩相接觸時間對釩反萃取率的影響。試驗結果錶明:對于釩質量濃度為17 g/L的釩淨化液,用10%7101+10%仲辛醇+80%煤油作萃取劑,在常溫、相比V o/V a=1/1條件下萃取5 min ,釩萃取率在90%以上,萃取劑飽和容量為29.5 g/L ;對于負載17.0 g/L釩的有機相,用170 g/L的(N H4)2 CO3溶液作反萃取劑反萃取沉澱釩,控製相比V o/V a =1/1,溫度為35~40℃,兩相接觸15 min ,釩的反萃取率達99%,所得五氧化二釩產品質量質量優于YB/T5304-2011冶金99級標準。
연구료용백알7101종범사침출액중췌취범,고찰료췌취제조성、량상접촉시간대범췌취솔적영향,이급반췌취제조성、온도급량상접촉시간대범반췌취솔적영향。시험결과표명:대우범질량농도위17 g/L적범정화액,용10%7101+10%중신순+80%매유작췌취제,재상온、상비V o/V a=1/1조건하췌취5 min ,범췌취솔재90%이상,췌취제포화용량위29.5 g/L ;대우부재17.0 g/L범적유궤상,용170 g/L적(N H4)2 CO3용액작반췌취제반췌취침정범,공제상비V o/V a =1/1,온도위35~40℃,량상접촉15 min ,범적반췌취솔체99%,소득오양화이범산품질량질량우우YB/T5304-2011야금99급표준。
The solvent extraction of vanadium using primary amine 7101 as extractant from vanadium slag leaching solution was studied .The effects of extractant composition and extraction time on extraction rate of vanadium ,and stripping agent composition ,temperature and contacting time on stripping rate of vanadium were examined .The results show that for the leaching solution which vanadium mass concentrate is 17 .0 g/L ,using 10% 7101+ 10% secoctyl alcohol + 80% kerosene as extractant ,vanadium extraction rate is over 90% under the conditions of 35 -40 ℃ ,Vo/Va = 1/1 , contacting time of 5 min .The extractant saturation capacity for vanadium is 29 .5 g/L .For the loading organic phase ,using 170 g/L (NH4 )2CO3 solution as stripping extractant to strip and precipitate vanadate ,under the conditions of room temperature ,V o/V a = 1/1 ,contacting time of 15 min ,the stripping rate of vanadium is over 99% ,and V2 O5 products quality is better than YB/T5304-2011 Metallurgical Grade 99 standard .