用硅烷偶联剂KH-590对纳米二氧化硅表面进行改性。考查了偶联剂用量、改性温度及时间对改性效果的影响。确定最佳改性条件为：硅烷偶联剂KH-590质量分数为5%，反应温度70℃，反应时间4h。并将改性后纳米二氧化硅用于聚硫密封剂中，提高了聚硫密封剂的耐老化和粘接性能。
용규완우련제KH-590대납미이양화규표면진행개성。고사료우련제용량、개성온도급시간대개성효과적영향。학정최가개성조건위：규완우련제KH-590질량분수위5%，반응온도70℃，반응시간4h。병장개성후납미이양화규용우취류밀봉제중，제고료취류밀봉제적내노화화점접성능。
The nano-silica surface was modified using silane coupling agent KH-590.The effect of modifier amount,modification temperature and time on the modification effect was investigated.The optimal modification conditions obtained were as follows:KH-590 content is 5%,reaction temperature is 70℃ and reaction time is 4 h.And the results indicated that the aging and bonding properties are improved by using modified nano-silica in the polysulfide sealants.