针对SiCp/Al的加工,提出一种超声振动磨削放电复合加工的方法,从加工效率、加工稳定性及表面质量等方面与电火花加工进行了对比试验研究。分析了两种加工方法的脉冲宽度和峰值电流对加工速度和表面粗糙度的影响,结果表明:电火花加工的表面粗糙度平均值为R a4.5μm,超声振动磨削放电复合加工的表面粗糙度平均值为Ra2μm;超声振动磨削放电复合加工的稳定性比电火花加工好,但加工速度较低。通过扫描电镜对两种加工方法下零件表面形貌和重熔层进行了观测,对试件表面进行了X射线衍射分析,表明采用超声振动磨削放电复合加工SiCp/Al复合材料可获得较好的表面质量。
針對SiCp/Al的加工,提齣一種超聲振動磨削放電複閤加工的方法,從加工效率、加工穩定性及錶麵質量等方麵與電火花加工進行瞭對比試驗研究。分析瞭兩種加工方法的脈遲寬度和峰值電流對加工速度和錶麵粗糙度的影響,結果錶明:電火花加工的錶麵粗糙度平均值為R a4.5μm,超聲振動磨削放電複閤加工的錶麵粗糙度平均值為Ra2μm;超聲振動磨削放電複閤加工的穩定性比電火花加工好,但加工速度較低。通過掃描電鏡對兩種加工方法下零件錶麵形貌和重鎔層進行瞭觀測,對試件錶麵進行瞭X射線衍射分析,錶明採用超聲振動磨削放電複閤加工SiCp/Al複閤材料可穫得較好的錶麵質量。
침대SiCp/Al적가공,제출일충초성진동마삭방전복합가공적방법,종가공효솔、가공은정성급표면질량등방면여전화화가공진행료대비시험연구。분석료량충가공방법적맥충관도화봉치전류대가공속도화표면조조도적영향,결과표명:전화화가공적표면조조도평균치위R a4.5μm,초성진동마삭방전복합가공적표면조조도평균치위Ra2μm;초성진동마삭방전복합가공적은정성비전화화가공호,단가공속도교저。통과소묘전경대량충가공방법하령건표면형모화중용층진행료관측,대시건표면진행료X사선연사분석,표명채용초성진동마삭방전복합가공SiCp/Al복합재료가획득교호적표면질량。
This paper presents a new method for machining SiCp/Al using a combination process of ultrasonic vibration assisted grinding with EDM. Comparative experiments of machining SiCp/Al by EDM and ultrasonic vibration assisted grinding with EDM were carried out. The effect of pulse width and peak current on machining speed and surface roughness in two machining methods was analyzed. The experimental results show that ultrasonic vibration assisted grinding with EDM can effectively reduce surface roughness, but the machining speed is low. Scanning electronic microscope was used to analyze the micro profiles of surface and test the thickness of re-melting layer, the X-ray diffractometer was used to detect the machining surfaces component. The observation results show that ultrasonic vibration assisted grinding with EDM could gain better surface quality of SiCp/Al.