刘雪静%谭洪生%李丽平%谭哲兴
劉雪靜%譚洪生%李麗平%譚哲興
류설정%담홍생%리려평%담철흥
连续纤维增强%玻璃纤维%浸渍带%力学性能
連續纖維增彊%玻璃纖維%浸漬帶%力學性能
련속섬유증강%파리섬유%침지대%역학성능
continuous fiber reinforced%glass fiber%prepreg tape%mechanical properties
分别以五种聚烯烃树脂为基体,采用自行设计的浸渍模具制备了连续玻璃纤维增强聚烯烃预浸带,并采用热模压机将预浸带压制成相应的板材。研究了五种基体树脂、纤维含量、纤维分布对复合材料力学性能的影响。结果表明,加入玻纤后复合材料的拉伸强度、弯曲强度大幅度提高,纤维分布对材料的弯曲性能影响较大;纤维含量0~70%范围内,随纤维用量的增加,复合材料的力学性能提高;在70%~75%范围内,复合材料的力学性能随纤维含量的增加而降低。动态力学分析表明,加入纤维后明显提高了复合材料的抗形变能力。
分彆以五種聚烯烴樹脂為基體,採用自行設計的浸漬模具製備瞭連續玻璃纖維增彊聚烯烴預浸帶,併採用熱模壓機將預浸帶壓製成相應的闆材。研究瞭五種基體樹脂、纖維含量、纖維分佈對複閤材料力學性能的影響。結果錶明,加入玻纖後複閤材料的拉伸彊度、彎麯彊度大幅度提高,纖維分佈對材料的彎麯性能影響較大;纖維含量0~70%範圍內,隨纖維用量的增加,複閤材料的力學性能提高;在70%~75%範圍內,複閤材料的力學性能隨纖維含量的增加而降低。動態力學分析錶明,加入纖維後明顯提高瞭複閤材料的抗形變能力。
분별이오충취희경수지위기체,채용자행설계적침지모구제비료련속파리섬유증강취희경예침대,병채용열모압궤장예침대압제성상응적판재。연구료오충기체수지、섬유함량、섬유분포대복합재료역학성능적영향。결과표명,가입파섬후복합재료적랍신강도、만곡강도대폭도제고,섬유분포대재료적만곡성능영향교대;섬유함량0~70%범위내,수섬유용량적증가,복합재료적역학성능제고;재70%~75%범위내,복합재료적역학성능수섬유함량적증가이강저。동태역학분석표명,가입섬유후명현제고료복합재료적항형변능력。
Five kinds of polyolefin resins were used as matrix ,the continuous glass fiber rein-forced polyolefin prepreg tapes were prepared by a self-designed impregnation mold and the prepreg tapes were pressed into the corresponding plate using a hot stamping press .The influ-ences of five kinds of polyolefin ,fiber content and fiber distribution on mechanical properties of composites were studied .The results show that the tensile and flexural strengths increase obvi-ously with the addition of the glass fibers ,and the influence of fiber distribution on flexural prop-erty of the composites was more obviously than that of other property .In the range of 0~70% , the mechanical properties of the composites increased with the increase of the fiber content .In the range of 70% ~75% ,the mechanical properties of the composites decreased with the increase of the fiber content .The result of dynamic mechanical behavior shows that the deformation re-sistance of the composites enhanced evidently with the increase of the glass fiber content .