中国钨业
中國鎢業
중국오업
CHINA TUNGSTEN INDUSTRY
2013年
5期
36-40
,共5页
左中眉%栾道成%田瀚林%陈晓男
左中眉%欒道成%田瀚林%陳曉男
좌중미%란도성%전한림%진효남
超细硬质合金%复式碳化物%压力烧结%TEM分析
超細硬質閤金%複式碳化物%壓力燒結%TEM分析
초세경질합금%복식탄화물%압력소결%TEM분석
ultrafine cemented carbides%composite carbides%pressure sintering%TEM analysis
以WC-6%Co和WC-8%Co为研究体系,在1390℃压力烧结下制备不同配比复式碳化物的超细硬质合金。分别采用洛氏硬度检测、抗弯强度检测、钴磁检测、矫顽磁力检测等方法,通过扫描电镜和电子衍射分析,研究了不同量的(W,Ti,Ta)C复式碳化物对超细硬质合金性能的影响。结果表明:WC-6%Co-2%(W,Ti,Ta)C超细硬质合金的矫顽磁力为45.39 kA·m-1,硬度为94.0 HRA,抗弯强度为2280 MPa;WC-8%Co-2%(W,Ti,Ta)C超细硬质合金的矫顽磁力为37.4 kA·m-1,硬度为93.4 HRA,抗弯强度为2670 MPa;WC-8%Co-2%(W,Ti,Ta)C-0.5%(Cr3C2/VC)的矫顽磁力为38.2 kA·m-1,硬度为93.6 HRA,抗弯强度为2780 MPa;它们具有较高的综合性能。
以WC-6%Co和WC-8%Co為研究體繫,在1390℃壓力燒結下製備不同配比複式碳化物的超細硬質閤金。分彆採用洛氏硬度檢測、抗彎彊度檢測、鈷磁檢測、矯頑磁力檢測等方法,通過掃描電鏡和電子衍射分析,研究瞭不同量的(W,Ti,Ta)C複式碳化物對超細硬質閤金性能的影響。結果錶明:WC-6%Co-2%(W,Ti,Ta)C超細硬質閤金的矯頑磁力為45.39 kA·m-1,硬度為94.0 HRA,抗彎彊度為2280 MPa;WC-8%Co-2%(W,Ti,Ta)C超細硬質閤金的矯頑磁力為37.4 kA·m-1,硬度為93.4 HRA,抗彎彊度為2670 MPa;WC-8%Co-2%(W,Ti,Ta)C-0.5%(Cr3C2/VC)的矯頑磁力為38.2 kA·m-1,硬度為93.6 HRA,抗彎彊度為2780 MPa;它們具有較高的綜閤性能。
이WC-6%Co화WC-8%Co위연구체계,재1390℃압력소결하제비불동배비복식탄화물적초세경질합금。분별채용락씨경도검측、항만강도검측、고자검측、교완자력검측등방법,통과소묘전경화전자연사분석,연구료불동량적(W,Ti,Ta)C복식탄화물대초세경질합금성능적영향。결과표명:WC-6%Co-2%(W,Ti,Ta)C초세경질합금적교완자력위45.39 kA·m-1,경도위94.0 HRA,항만강도위2280 MPa;WC-8%Co-2%(W,Ti,Ta)C초세경질합금적교완자력위37.4 kA·m-1,경도위93.4 HRA,항만강도위2670 MPa;WC-8%Co-2%(W,Ti,Ta)C-0.5%(Cr3C2/VC)적교완자력위38.2 kA·m-1,경도위93.6 HRA,항만강도위2780 MPa;타문구유교고적종합성능。
Composite carbides of different contents were doped in ultrafine cemented carbides based on WC-6%Co and WC-8 %Co by sintering the ultrafine cemented carbides in pressure at 1 390 ℃. The effects of (W,Ti,Ta)C composite carbides on the microstructure and mechanical properties of the ultrafine cemented carbides were analyzed by Rockwell Hardness Test, bending strength test, cobalt magnetic detection, coercive force test, SEM analysis, TEM analysis and other methods. The results indicate that the WC-6 %Co-2 %(W,Ti,Ta)C cemented carbide has coercive force of 45.39 kA·m-1 (hardness=94.0 HRA, TRS=2 280 MPa). The WC-8%Co-2%(W,Ti,Ta) C cemented carbide has coercive force of 37.4 kA·m-1 (hardness=93.4 HRA, TRS=2 670 MPa). WC-8%Co-2%(W,Ti,Ta)C-0.5%(Cr3C2/VC) cemented carbide has coercive force of 38.2 kA·m-1 (hardness=93.6 HRA, TRS=2 780 MPa). These ultra-fine cemented carbides have favorable comprehensive properties.