混凝土与水泥制品
混凝土與水泥製品
혼응토여수니제품
CHINA CONCRETE AND CEMENT PRODUCTS
2013年
10期
19-24
,共6页
肖佳%郭明磊%许彩云%孟庆业
肖佳%郭明磊%許綵雲%孟慶業
초가%곽명뢰%허채운%맹경업
水泥-石灰石粉胶凝材料%粉煤灰%干缩性能%开裂性能
水泥-石灰石粉膠凝材料%粉煤灰%榦縮性能%開裂性能
수니-석회석분효응재료%분매회%간축성능%개렬성능
Cement-ground limestone cementitious material%Fly ash%Drying shrinkage property%Cracking property
研究了水泥-石灰石粉胶凝材料干缩和开裂性能以及粉煤灰对其干缩和开裂性能的改善作用。研究得到水泥-石灰石粉胶凝材料的干缩随石灰石粉掺量增加出现先增大后减小的规律,石灰石粉掺量为10%时,硬化浆体的干缩达到最大值。随粉煤灰掺量增加,水泥-石灰石粉硬化浆体的干缩随之减少。随石灰石粉掺量增加,水泥-石灰石粉胶凝材料的开裂呈现先增大后减小的规律,掺量为10%时的开裂最大;随粉煤灰掺量增加,粉煤灰对水泥-石灰石粉胶凝材料开裂性能的改善逐渐增强。水泥-石灰石粉胶凝材料的开裂性能与其干缩性能有着较大的相关性,干缩减少,其开裂指数逐渐降低,抗开裂性能提高。
研究瞭水泥-石灰石粉膠凝材料榦縮和開裂性能以及粉煤灰對其榦縮和開裂性能的改善作用。研究得到水泥-石灰石粉膠凝材料的榦縮隨石灰石粉摻量增加齣現先增大後減小的規律,石灰石粉摻量為10%時,硬化漿體的榦縮達到最大值。隨粉煤灰摻量增加,水泥-石灰石粉硬化漿體的榦縮隨之減少。隨石灰石粉摻量增加,水泥-石灰石粉膠凝材料的開裂呈現先增大後減小的規律,摻量為10%時的開裂最大;隨粉煤灰摻量增加,粉煤灰對水泥-石灰石粉膠凝材料開裂性能的改善逐漸增彊。水泥-石灰石粉膠凝材料的開裂性能與其榦縮性能有著較大的相關性,榦縮減少,其開裂指數逐漸降低,抗開裂性能提高。
연구료수니-석회석분효응재료간축화개렬성능이급분매회대기간축화개렬성능적개선작용。연구득도수니-석회석분효응재료적간축수석회석분참량증가출현선증대후감소적규률,석회석분참량위10%시,경화장체적간축체도최대치。수분매회참량증가,수니-석회석분경화장체적간축수지감소。수석회석분참량증가,수니-석회석분효응재료적개렬정현선증대후감소적규률,참량위10%시적개렬최대;수분매회참량증가,분매회대수니-석회석분효응재료개렬성능적개선축점증강。수니-석회석분효응재료적개렬성능여기간축성능유착교대적상관성,간축감소,기개렬지수축점강저,항개렬성능제고。
The drying shrinkage and cracking property of the cement-ground limestone cementitious material and the improvement of fly ash on the drying shrinkage and cracking property of the cement-ground limestone cementitious mate≥rial are studied. The results show that the drying shrinkage of the cement-ground limestone cementitious material increas≥es at first and decreases later with the ground limestone content increasing, which reaches the maximum when ground limestone content is 10%. The drying shrinkage of the cement-ground limestone cementitious material decreases with the fly ash content increasing. The cracking of the cement-ground limestone cementitious material increases at first and de≥creases later with the ground limestone content increasing, which reaches the biggest cracking at the ground limestone content of 10%. The increase of the fly ash content boosts the improvement of the fly ash on the cracking property of the cement-ground limestone cementitious material. The drying shrinkage and cracking property of the cement-ground lime≥stone cementitious material have a lot of correlation, the decrease of drying shrinkage corresponds to the reduction of the cracking index and the improvement of anti-cracking property.